P. Zavalij, Wei Bao, X. F. Wang, J. J. Ying, X. H. Chen, D. M. Wang, J. B. He, X. Q. Wang, G. F. Chen, P.-Y. Hsieh, Q. Huang, M. A. Green
DOI 10.1103/PhysRevB.83.132509 · Physical Review B
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
With single-crystal x-ray diffraction studies, we compare the structures of three samples showing optimal superconductivity: K0.775(4)Fe1.613(1)Se2, K0.737(6)Fe1.631(3)Se2, and Cs0.748(2)Fe1.626(1)Se2. All have an almost identical ordered vacancy structure with a (5 × 5 × 1) supercell. The tetragonal unit cell, space group I4/m, possesses lattice parameters at 250 K of a = b = 8.729(2) Å and c = 14.120(3) Å, a = b = 8.7186(12) Å and c = 14.0853(19) Å, and at 295 K, a = b = 8.8617(16) Å and c = 15.304(3) Å for the three crystals, respectively. The structure contains two iron sites; one is almost completely empty while the other is fully occupied. There are similarly two alkali metal sites that are occupied in the range of 72.2(2)%–85.3(3)%. The inclusion of alkali metals and the presence of vacancies within the structure allows for considerable relaxation of the FeSe4 tetrahedron, compared with members of the Fe(Te, Se, S) series, and the resulting shift of the Se–Fe–Se bond angles to less distorted geometry could be important in understanding the associated increase in the superconducting transition temperature. The structure of these superconductors are distinguished from the structure of the nonsuperconducting phases by an almost complete absence of Fe on the (0 0.5 0.25) site, as well as lower alkali metal occupancy that ensures an exact Fe2+ oxidation state, which are clearly critical parameters in the promotion of superconductivity.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| K0.775Fe1.613Se2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 32 | Pressure not reported | unknown |
| K0.737Fe1.631Se2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 32 | Pressure not reported | unknown |
| Cs0.748Fe1.626Se2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 32 | Pressure not reported | unknown |
| FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 8.5 | Pressure not reported | unknown |
Similar papers
On the Structure of Vacancy Ordered Superconducting Alkali Metal Iron Selenide
similarity 0.99P. Zavalij et al. · 2011 · arXiv:1101.4882
Source status unknown — claims are unverified
Coexistence of different electronic phases in the K0.8Fe1.6Se2 superconductor: A bulk-sensitive hard x-ray spectroscopy study
similarity 0.95L. Simonelli et al.
Source status unknown — claims are unverified
Robustness of superconducting properties to transition metal substitution and impurity phases in Fe1−xVxSe
similarity 0.95Franziska K. K. Kirschner et al.
Source status unknown — claims are unverified
Superconductivity in FeSe: The Role of Nematic Order
similarity 0.95Jian Kang et al.
Source status unknown — claims are unverified
Bulk Superconductivity and Role of Fluctuations in the Iron-Based Superconductor FeSe at High Pressures
similarity 0.95Elena Gati et al.
Source status unknown — claims are unverified
Elucidating the magnetic and superconducting phases in the alkali metal intercalated iron chalcogenides
similarity 0.95Meng Wang et al.
Source status unknown — claims are unverified