Angular slippage from the crystallographic c axis of the reversible magnetization vector in a tilted crystal of a highly anisotropic cuprate superconductor

Abstract

The magnetization vector M⃗ was measured in the reversible region of the mixed state of a high-quality Tl2Ba2Ca2Cu3O10 single crystal as a function of temperature and for different magnetic field amplitudes and orientations. These measurements allowed to study the M⃗ components perpendicular and parallel to the CuO2 layers (M⊥ and M∥, respectively) under arbitrary values for the corresponding components of the applied magnetic field, H⊥ and H∥. For temperatures close to Tc (in the critical fluctuation region), we observed M⊥(H⊥,H∥)≈M⊥(H⊥,0) and M∥(H⊥,H∥)≈0, as expected for an extremely anisotropic material. However, deviations from this behavior are observed at lower temperatures in the London region. In particular, the M⊥ amplitude under a constant H⊥ decreases on increasing H∥. In turn, in spite of the experimental uncertainties affecting M∥ (mainly associated with the rotating sample holder), its amplitude under a constant H∥ becomes observable on increasing H⊥. Both effects lead to an angular slippage of the magnetization vector M⃗ from the c crystallographic axis when the applied magnetic field is tilted from that axis. The M⊥ behavior is phenomenologically explained in the framework of Lawrence-Doniach approaches for single layered superconductors by just assuming a slight angular dependence of the so-called vortex structure constant. However, the observed M∥ is orders of magnitude larger than expected, a fact that is related to the multilayered nature of the compound studied. Our present results also directly affect the interpretation of recent measurements of the magnetic torque in other extremely anisotropic high-Tc cuprates.

Source-reported materials — not catalogue approval

Similar papers