Andreev reflection and spin polarization measurement of Co/YBCO junction

N. Ghosh, J. Barzola Quiquia, Q. Xu, G. Biehne, H. Hochmuth, M. Lorenz M. Grundmann, H. Schmidt

arXiv:0804.0170 · 2008-04-01 · arXiv: Superconductivity

T2theoretical

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

We report temperature dependent Andreev reflection measurements of Co/ Y$_{1}$Ba$_{2}$Cu$_{3}$O$_{7-δ}$ (YBCO) heterostructure samples with junction areas of 1 $μ$m diameter. Modelling of the 5-70 K conductivity data according to a modified Blonder-Tinkham-Klapwijk theory yields a spin polarization in Co film amounting to 34% which is almost constant up to 70 K. The YBCO films have been grown by pulsed laser deposition on sapphire substrates. The Co films are deposited by thermal evaporation on YBCO. The film is characterized by powder X-ray diffraction measurements which shows YBCO is grown in (001) direction.The critical current density, 5 x 10$^{6}$ A/cm$^{2}$, in YBCO remains nearly constant after deposition of Co at zero field and 77 K.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
Y1Ba2Cu3O7-δ Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	92	Pressure unresolved	unknown