Superconductivity at 41.0 K in the F-doped LaFeAsO1-xFx
Wei Lu, Xiao-Li Shen, Jie Yang, Zheng-Cai Li, Wei Yi, Zhi-An Ren, Xiao-Li Dong, Guang-Can Che, Li-Ling Sun, Fang Zhou, Zhong-Xian Zhao
arXiv:0804.3725 · DOI 10.1016/j.ssc.2008.07.032 · 2008-04-23 · Solid State Communications
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Here we report the superconductivity in the LaFeAsO1-xFx system prepared by high pressure synthesis. The highest onset superconducting transition temperature (Tc) in this La-based system is 41.0 K with the nominal composition of LaFeAsO1-xFx (x = 0.6), which is higher than that reported previously by ambient pressure synthesis. The increase of Tc can be attributed to the further shrinkage of crystal lattice that causes the stronger chemical pressure on the Fe-As plane, which is induced by the increased F-doping level under high pressure synthesis.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| LaFeAsO0.4F0.6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 41 | Pressure not reported | onset |
Similar papers
Superconductivity at 43 K at ambient pressure in the iron-based layered compound La1−xYxFeAsOy
similarity 0.91Parasharam M. Shirage et al.
Source status unknown — claims are unverified
Synthesis and Microstructural Studies of Iron Based LaO1-xFxFeAs Superconducting Materials
similarity 0.91Chandra Shekhar et al. · 2008 · arXiv:0806.1661
Source status unknown — claims are unverified
La-substituted CaFeAsH superconductor with Tc = 47 K
similarity 0.90Yoshinori Muraba et al. · 2013 · arXiv:1401.0097
Source status unknown — claims are unverified
Superconductivity at 52 K in iron-based F-doped layered quaternary compound Pr[O1-xFx]FeAs
similarity 0.89Zhi-An Ren et al. · 2008 · arXiv:0803.4283
Source status unknown — claims are unverified
Superconductivity in La-Ba-Cu-O metallic oxide compounds above 50 K
similarity 0.88I. Kirschner et al.
Source status unknown — claims are unverified
Superconductivity at 41 K and Its Competition with Spin-Density-Wave Instability in Layered CeO1−xFxFeAs
similarity 0.88G. F. Chen et al.
Source status unknown — claims are unverified