Thorium-doping induced superconductivity up to 56 K in Gd1-xThxFeAsO

Cao Wang; Linjun Li; Shun Chi; Zengwei Zhu; Zhi Ren; Yuke Li; Yuetao Wang; Xiao Lin; Yongkang Luo; Shuai Jiang; Xiangfan Xu; Guanghan Cao; Zhu'an Xu

doi:10.1209/0295-5075/83/67006

Thorium-doping induced superconductivity up to 56 K in Gd1-xThxFeAsO

Cao Wang, Linjun Li, Shun Chi, Zengwei Zhu, Zhi Ren, Yuke Li, Yuetao Wang, Xiao Lin, Yongkang Luo, Shuai Jiang, Xiangfan Xu, Guanghan Cao, Zhu'an Xu

arXiv:0804.4290 · DOI 10.1209/0295-5075/83/67006 · 2008-04-28 · EPL (Europhysics Letters)

T1theoretical487 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Following the discovery of superconductivity in an iron-based arsenide LaO1-xFxFeAs with a superconducting transition temperature (Tc) of 26 K[1], Tc was pushed up surprisingly to above 40 K by either applying pressure[2] or replacing La with Sm[3], Ce[4], Nd[5] and Pr[6]. The maximum Tc has climbed to 55 K, observed in SmO1-xFxFeAs[7, 8] and SmFeAsO1-x[9]. The value of Tc was found to increase with decreasing lattice parameters in LnFeAsO1-xFx (Ln stands for the lanthanide elements) at an apparently optimal doping level. However, the F- doping in GdFeAsO is particularly difficult[10,11] due to the lattice mismatch between the Gd2O2 layers and Fe2As2 layers. Here we report observation of superconductivity with Tc as high as 56 K by the Th4+ substitution for Gd3+ in GdFeAsO. The incorporation of relatively large Th4+ ions relaxes the lattice mismatch, hence induces the high temperature superconductivity.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
LaO1-xFxFeAs Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	26	Pressure not reported	unknown
SmO1-xFxFeAs Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	55	Pressure not reported	unknown
SmFeAsO1-x Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	55	Pressure not reported	unknown
GdO0.83F0.17FeAs Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	36	Pressure not reported	unknown
GdFeAsO1-x Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	53.5	Pressure not reported	unknown
Gd0.8Th0.2FeAsO Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	56	Pressure not reported	unknown
Gd0.8Th0.2FeAsO Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	56.3	Pressure not reported	onset
Gd0.75Th0.25FeAsO Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	55	Pressure not reported	zero_resistance