Transport properties and superconductivity in $Ba_{1-x}M_xFe_2As_2$ (M=La and K) with double FeAs layers

G. Wu; R. H. Liu; H. Chen; Y. J. Yan; T. Wu; Y. L. Xie; J. J. Ying; X. F. Wang; D. F. Fang; X. H. Chen

doi:10.1209/0295-5075/84/27010

← Back to search

Transport properties and superconductivity in $Ba_{1-x}M_xFe_2As_2$ (M=La and K) with double FeAs layers

G. Wu, R. H. Liu, H. Chen, Y. J. Yan, T. Wu, Y. L. Xie, J. J. Ying, X. F. Wang, D. F. Fang, X. H. Chen

arXiv:0806.1459 · DOI 10.1209/0295-5075/84/27010 · 2008-06-09 · EPL (Europhysics Letters)

T1theoretical61 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

We synthesized the samples $Ba_{1-x}M_xFe_2As_2$ (M=La and K) with $ThCr_2Si_2$-type structure. These samples were systematically characterized by resistivity, thermoelectic power (TEP) and Hall coefficient ($R_H$). $BaFe_2As_2$ shows an anomaly in resistivity at about 140 K. Substitution of La for Ba leads to a shift of the anomaly to low temperature, but no superconducting transition is observed. Potassium doping leads to suppression of the anomaly in resistivity and induces superconductivity at 38 K as reported by Rotter et al.\cite{rotter}. The Hall coefficient and TEP measurements indicate that the TEP is negative for $BaFe_2As_2$ and La-doped $BaFe_2As_2$, indicating n-type carrier; while potassium doping leads to change of the sign in $R_H$ and TEP. It definitely indicates p-type carrier in superconducting $Ba_{1-x}K_xFe_2As_2$ with double FeAs layers, being in contrast to the case of $LnO_{1-x}F_xFeAs$ with single FeAs layer. A similar superconductivity is also observed in the sample with nominal composition $Ba_{1-x}K_xOFe_2As_2$.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
Ba1-xKxFe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	38	Pressure not reported	unknown
LaO1-xFxFeAs Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	26	Pressure not reported	unknown
SmO1-xFxFeAs Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	43	Pressure not reported	unknown
CeO1-xFxFeAs Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	41	Pressure not reported	unknown
PrO1-xFxFeAs Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	52	Pressure not reported	unknown
Ba0.6K0.4Fe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	38	Pressure not reported	unknown
Ba0.5K0.5OFe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	36	Pressure not reported	unknown
Ba0.5K0.5OFe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	36	Pressure not reported	unknown
Ba0.6K0.4Fe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	38	Pressure not reported	unknown