Upper critical field, anisotropy, and superconducting properties of Ba$_{1-x}$K$_x$Fe$_2$As$_2$ single crystals

Zhao-Sheng Wang; Hui-Qian Luo; Cong Ren; Hai-Hu Wen

doi:10.1103/PhysRevB.78.140501

← Back to search

Upper critical field, anisotropy, and superconducting properties of Ba$_{1-x}$K$_x$Fe$_2$As$_2$ single crystals

Zhao-Sheng Wang, Hui-Qian Luo, Cong Ren, Hai-Hu Wen

arXiv:0808.2392 · DOI 10.1103/PhysRevB.78.140501 · 2008-08-18 · Physical Review B

T1theoretical98 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

The temperature dependent resistivity of Ba$_{1-x}$K$_x$Fe$_2$As$_2$ (x = 0.23, 0.25, 0.28 and 0.4) single crystals and the angle dependent resistivity of superconducting Ba$_{0.6}$K$_{0.4}$Fe$_2$As$_2$ single crystals were measured in magnetic fields up to 9 T. The measurements of temperature dependent resistivity for samples with different doping levels revealed very high upper critical fields which increase with the transition temperature monotonously, and a very low superconducting anisotropy ratio $Γ=H_{c2}^{ab}/H_{c2}^c \approx$ 2. By scaling the resistivity in the frame of the anisotropic Ginzburg-Landau theory, the angle dependent resistivity of the Ba$_{0.6}$K$_{0.4}$Fe$_2$As$_2$ single crystal measured with different magnetic fields at a certain temperature collapsed onto one curve. As the only scaling parameter, the anisotropy $Γ$ was determined alternatively for each temperature and was found to be between two and three.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
LaFeAsO1-xFx Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	26	Pressure not reported	unknown
SmFeAsO1-xFx Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	55	Pressure not reported	unknown
Ba0.77K0.23Fe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	24	Pressure unresolved	onset
Ba0.75K0.25Fe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	28.3	Pressure unresolved	onset
Ba0.72K0.28Fe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	31.7	Pressure unresolved	onset
Ba0.6K0.4Fe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	36.5	Pressure unresolved	onset
Ba0.6K0.4Fe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	36.5	Pressure unresolved	unknown
Ba0.6K0.4Fe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	36.5	Pressure unresolved	onset
Ba0.6K0.4Fe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	36.5	Pressure unresolved	onset