Anisotropic magnetic and superconducting properties of aligned weak-ferromagnetic superconductor RuSr$_2$RCu$_2$O$_8$ (R = rare earths)

B. C. Chang, C. H. Hsu, M. F. Tai, H. C. Ku, Y. Y. Hsu

arXiv:0811.3457 · 2008-11-21 · arXiv: Superconductivity

T2experimental

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

The powder alignment method is used to investigate the anisotropic physical properties of the weak-ferromagnetic superconductor system RuSr2RCu2O8 (R = Pr, Nd, Sm, Eu, Gd, Gd0.5Dy0.5). The RuSr2GdCu2O8 cuprate is a weak-ferromagnetic superconductor with a magnetic ordering of Ru moments at TN(Ru) = 131 K, a superconducting transition in the CuO2 layers at Tc = 56 K, and a low temperature Gd antiferromagnetic ordering at TN(Gd) = 2.5 K. Due to weak magnetic anisotropy of this tetragonal system, highly c-axis aligned microcrystalline powder (diameter ~ 1-10 $μ$m) in epoxy can be obtained only for R = Eu and Gd through the field-rotation powder alignment method where c-axis is perpendicular to the aligned magnetic field Ba = 0.9 T and parallel to the rotation axis. For smaller rare earth compound R = Gd0.5Dy0.5, powder alignment can be achieved using the simple field powder alignment method where c-axis is partially aligned along the aligned magnetic field. The anisotropic temperature dependence of magnetic susceptibility for the c-axis aligned powders exhibit weak anisotropy with $χ_{c} > χ_{ab}$ at room temperature due to anisotropic rare earth, Eu and Gd, contribution and crossover to $χ_{c} < χ_{ab}$ below 190 K where strong Ru anisotropic short-range exchange interaction overtakes the rare earth contribution. Anisotropic diamagnetic superconducting intragrain shielding signal of aligned microcrystalline RuSr2GdCu2O8 powder-in-epoxy below vortex lattice melting temperature at 39 K in 1-G field is much weaker than the intergrain polycrystalline bulk sample signal due to the small grain size (d ~ 1-10 $μ$m), long penetration depth ($λ_{ab}$ ~ 0.55 $μ$m, $λ_{c}$ ~ 0.66 $μ$m) and the two-dimensional (2D) character of CuO2 layers.

Source-reported materials — not catalogue approval

FormulaReported Tc (K)Pressure (GPa)Type
RuSr2GdCu2O8

Archive — visibility unverified

Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.

56Pressure not reportedonset
RuSr2GdCu2O8

Archive — visibility unverified

Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.

39Pressure not reportedunknown
RuSr2GdCu2O8

Archive — visibility unverified

Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.

60Pressure not reportedonset
RuSr2SmCu2O8

Archive — visibility unverified

Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.

0Pressure not reportedonset
RuSr2EuCu2O8

Archive — visibility unverified

Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.

36Pressure not reportedonset
RuSr2Gd0.5Dy0.5Cu2O8

Archive — visibility unverified

Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.

55Pressure not reportedonset
RuSr2EuCu2O8

Archive — visibility unverified

Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.

21Pressure not reportedzero_resistance

Similar papers