Superconducting properties of the oxygen-vacant iron oxyarsenide TbFeAsO1-x from underdoped to overdoped compositions
Y. G. Shi, S. Yu, A. A. Belik, Y. Matsushita, M. Tanaka, Y. Katsuya, K. Kobayashi, Y. Hata, H. Yasuoka, K. Yamaura, E. Takayama-Muromachi
arXiv:0812.4907 · DOI 10.1103/PhysRevB.80.104501 · 2008-12-29 · Physical Review B
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
A wide-range doping was achieved by a high-pressure method for TbFeAsO1-x from "under doped" to "over doped" superconducting compositions throughout the optimized superconductivity (Tc of 44 K). Tc vs. lattice constant shows a dome-shaped feature, while Tc vs. the lattice constant likely follows a unique empirical curve over the doping range. The relatively large amount of oxygen vacancies up to 0.3 per the formula unit was introduced possibly because of the smaller replacement Tb than the other Ln (rare-earth element) in the LnFeAsO1-x system.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| TbFeAsO1-x Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 44 | Pressure not reported | unknown |
Similar papers
Superconducting properties of the oxygen-deficient iron oxyarsenide TbFeAsO1−δ from underdoped to overdoped compositions
similarity 0.99Y. G. Shi et al.
Source status unknown — claims are unverified
Synthesis and superconducting properties of the iron oxyarsenide TbFeAsO0.85
similarity 0.93Y. G. Shi et al. · 2008 · arXiv:0808.1948
Source status unknown — claims are unverified
Hydrogen in layered iron arsenides: Indirect electron doping to induce superconductivity
similarity 0.89Taku Hanna et al.
Source status unknown — claims are unverified
Superconductivity at 43 K at ambient pressure in the iron-based layered compound La1−xYxFeAsOy
similarity 0.88Parasharam M. Shirage et al.
Source status unknown — claims are unverified
Controlling factors of Tc dome structure in 1111-type iron arsenide superconductors
similarity 0.88Satoru Matsuishi et al.
Source status unknown — claims are unverified
Controlling Factors of Tc-Dome Structure in 1111-Type Iron Arsenide Superconductors
similarity 0.88Satoru Matsuishi et al. · 2013 · arXiv:1312.6747
Source status unknown — claims are unverified