Neutron Irradiation of Sm-1111

M. Eisterer, H. W. Weber, J. Jiang, J. D. Weiss, A. Yamamoto, A. A. Polyanskii, E. E. Hellstrom, D. C. Larbalestier

arXiv:0904.2442 · DOI 10.1088/0953-2048/22/6/065015 · 2009-04-16 · Superconductor Science and Technology

T1theoretical18 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

SmFeAsO$_{1-x}$F$_x$ was irradiated in a fission reactor to a fast (E > 0.1 MeV) neutron fluence of 4x10^${21}$ m$^{-2}$. The introduced defects increase the normal state resistivity due to a reduction in the mean free path of the charge carriers. This leads to an enhancement of the upper critical field at low temperatures. The critical current density within the grains, Jc, increases upon irradiation. The second maximum in the field dependence of Jc disappears and the critical current density becomes a monotonically decreasing function of the applied magnetic field.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
SmFeAsO1-xFx Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	53.6	Pressure not reported	onset
SmFeAsO1-xFx Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	53.2	Pressure not reported	onset