Nature of the Magnetic Order in BaMn2As2

Yogesh Singh; M. A. Green; Q. Huang; A. Kreyssig; R. J. McQueeney; D. C. Johnston; A. I. Goldman

doi:10.1103/PhysRevB.80.100403

← Back to search

Nature of the Magnetic Order in BaMn2As2

Yogesh Singh, M. A. Green, Q. Huang, A. Kreyssig, R. J. McQueeney, D. C. Johnston, A. I. Goldman

arXiv:0907.4094 · DOI 10.1103/PhysRevB.80.100403 · 2009-07-23 · Physical Review B

T315 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Neutron diffraction measurements have been performed on a powder sample of BaMn2As2 over the temperature T range from 10 K to 675 K. These measurements demonstrate that this compound exhibits collinear antiferromagnetic ordering below the Neel temperature T_N = 625(1) K. The ordered moment mu = 3.88(4) mu_B/Mn at T = 10 K is oriented along the c axis and the magnetic structure is G-type, with all nearest-neighbor Mn moments antiferromagnetically aligned. The value of the ordered moment indicates that the oxidation state of Mn is Mn^{2+} with a high spin S = 5/2. The T dependence of mu suggests that the magnetic transition is second-order in nature. In contrast to the closely related AFe2As2 (A = Ca, Sr, Ba, Eu) compounds, no structural distortion is observed in the magnetically ordered state of BaMn2As2.