Thickness-induced insufficient oxygen reduction in La(2-x)CexCuO4 thin films

B. X. Wu; K. Jin; J. Yuan; H. B. Wang; T. Hatano; B. R. Zhao; B. Y. Zhu

doi:10.1088/0953-2048/22/8/085004

← Back to search

Thickness-induced insufficient oxygen reduction in La(2-x)CexCuO4 thin films

B. X. Wu, K. Jin, J. Yuan, H. B. Wang, T. Hatano, B. R. Zhao, B. Y. Zhu

arXiv:0908.2211 · DOI 10.1088/0953-2048/22/8/085004 · 2009-08-16 · Superconductor Science and Technology

T36 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

A series of electron-doped cuprate La(2-x)CexCuO4 thin films with different thicknesses have been fabricated and their annealing time are adjusted carefully to ensure the highest superconducting transition temperature. The transport measurements indicate that, with the increase of the film thickness (<100 nm), the residual resistivity increases and the Hall coefficient shifts in the negative direction. Further more, the X-ray diffraction data reveal that the c-axis lattice constant c0 increases with the decrease of film thickness. These abnormal phenomena can be attributed to the insufficient oxygen reduction in the thin films. Considering the lattice mismatching in the ab-plane between the SrTiO3 substrates and the films, the compressive stress from the substrates may be responsible for the more difficult reduction of the oxygen in the thin films.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
La1.895Ce0.105CuO4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	21.5	Pressure not reported	zero_resistance
La1.895Ce0.105CuO4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	26.5	Pressure not reported	onset
La1.895Ce0.105CuO4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	26	Pressure not reported	zero_resistance
La1.895Ce0.105CuO4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	27.5	Pressure not reported	onset
La1.895Ce0.105CuO4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	26.5	Pressure not reported	zero_resistance
La1.895Ce0.105CuO4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	28	Pressure not reported	onset
La1.895Ce0.105CuO4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	26.5	Pressure not reported	zero_resistance
La1.895Ce0.105CuO4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	28	Pressure not reported	onset
La1.895Ce0.105CuO4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	27.3	Pressure not reported	zero_resistance
La1.895Ce0.105CuO4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	28.5	Pressure not reported	onset
La1.895Ce0.105CuO4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	27	Pressure not reported	zero_resistance
La1.895Ce0.105CuO4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	28.5	Pressure not reported	onset