Origin of critical-temperature enhancement of an iron-based high-T_c superconductor, LaFeAsO_{1-x}F_{x} : NMR study under high pressure

T. Nakano; N. Fujiwara; K. Tatsumi; H. Okada; H. Takahashi; Y. Kamihara; M. Hirano; H. Hosono

doi:10.1103/PhysRevB.81.100510

← Back to search

Origin of critical-temperature enhancement of an iron-based high-T_c superconductor, LaFeAsO_{1-x}F_{x} : NMR study under high pressure

T. Nakano, N. Fujiwara, K. Tatsumi, H. Okada, H. Takahashi, Y. Kamihara, M. Hirano, H. Hosono

arXiv:0909.0318 · DOI 10.1103/PhysRevB.81.100510 · 2009-09-02 · Physical Review B

T1theoretical19 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Nuclear magnetic resonance (NMR) measurements of an iron (Fe)-based superconductor LaFeAsO_{1-x}F_x (x = 0.08 and 0.14) were performed at ambient pressure and under pressure. The relaxation rate 1/T_1 for the overdoped samples (x = 0.14) shows T-linear behavior just above T_c, and pressure application enhances 1/T_1T similar to the behavior of T_c. This implies that 1/T_1T = constant originates from the Korringa relation, and an increase in the density of states at the Fermi energy D(E_F) leads to the enhancement of T_c. In the underdoped samples (x = 0.08), 1/T_1T measured at ambient pressure also shows T-independent behavior in a wide temperature range above T_c. However, it shows Curie-Weiss-like T dependence at 3.0 GPa accompanied by a small increase in T_c, suggesting that predominant antiferromagnetic fluctuation suppresses development of superconductivity or remarkable enhancement of T_c. The qualitatively different features between underdoped and overdoped samples are systematically explained by a band calculation with hole and electron pockets.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
LaFeAsO1-xFx Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	26	Pressure unresolved	unknown
LaFeAsO1-xFx Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	43	4.5 GPa	unknown
LaFeAsO1-xFx Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	20	Pressure unresolved	unknown
LaFeAsO1-xFx Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	43	4.5 GPa	unknown
LaFeAsO1-xFx Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	30	Pressure not reported	unknown