Superconductivity at 15.6 K in Calcium-doped Tb_{1-x}Ca_xFeAsO: the structure requirement for achieving superconductivity in the hole-doped 1111 phase
Gang Mu, Bin Zeng, Peng Cheng, Xiyu Zhu, Fei Han, Bing Shen, Hai-Hu Wen
arXiv:0909.5571 · DOI 10.1209/0295-5075/89/27002 · 2009-09-30
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Superconductivity at about 15.6 K was achieved in Tb_{1-x}Ca_xFeAsO by partially substituting Tb^{3+} with Ca^{2+} in the nominal doping region x = 0.40 \sim 0.50. A detailed investigation was carried out in a typical sample with doping level of x = 0.44. The upper critical field of this sample was estimated to be 77 Tesla from the magnetic field dependent resistivity data. The domination of hole-like charge carriers in the low-temperature region was confirmed by Hall effect measurements. The comparison between the calcium-doped sample Pr_{1-x}Ca_xFeAsO (non-superconductive) and the Strontium-doped sample Pr_{1-x}Sr_xFeAsO (superconductive) suggests that a lager ion radius of the doped alkaline-earth element compared with that of the rare-earth element may be a necessary requirement for achieving superconductivity in the hole-doped 1111 phase.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| Tb0.56Ca0.44FeAsO Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 15.6 | Pressure not reported | onset |
| Tb0.56Ca0.44FeAsO Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 15.6 | Pressure not reported | onset |
Similar papers
Superconductivity induced by Ni doping in BaFeAs
similarity 0.91L. J. Li et al. · 2008 · arXiv:0809.2009
Source status unknown — claims are unverified
To What Extent Iron-Pnictide New Superconductors Have Been Clarified: A Progress Report
similarity 0.90Kenji Ishida et al. · 2009 · arXiv:0906.2045
Source status unknown — claims are unverified
Suppression of superconductivity and structural phase transition against pressure in Ca(IrAs)(FeIrAs)
similarity 0.90Shunsaku Kitagawa et al. · 2014 · arXiv:1412.2317
Source status unknown — claims are unverified
Superconductivity above 50 K in TbThFeAsO
similarity 0.90Lin-jun Li et al. · 2008 · arXiv:0806.1675
Source status unknown — claims are unverified
Superconductivity in hole-doped (SrK)FeAs
similarity 0.89G. F. Chen et al. · 2008 · arXiv:0806.1209
Source status unknown — claims are unverified
Synthesis, structural and transport properties of the hole-doped Superconductor Pr_{1-x}Sr_xFeAsO
similarity 0.89Gang Mu et al. · 2008 · arXiv:0810.0986
Source status unknown — claims are unverified