Effect of magnetic field on the spin resonance in FeTe(0.5)Se(0.5) as seen via inelastic neutron scattering

Wen, Jinsheng; Xu, Guangyong; Xu, Zhijun; Lin, Zhi Wei; Li, Qiang; Chen, Ying; Chi, Songxue; Gu, Genda; Tranquada, J. M.

Effect of magnetic field on the spin resonance in FeTe(0.5)Se(0.5) as seen via inelastic neutron scattering

Wen, Jinsheng, Xu, Guangyong, Xu, Zhijun, Lin, Zhi Wei, Li, Qiang, Chen, Ying, Chi, Songxue, Gu, Genda, Tranquada, J. M.

arXiv:0910.0027 · 2010-03-30

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Inelastic neutron scattering and susceptibility measurements have been performed on the optimally-doped Fe-based superconductor FeTe(0.5)Se(0.5), which has a critical temperature, Tc of 14 K. The magnetic scattering at the stripe antiferromagnetic wave-vector Q = (0.5,0.5) exhibits a "resonance" at ~ 6 meV, where the scattering intensity increases abruptly when cooled below Tc. In a 7-T magnetic field parallel to the a-b plane, Tc is slightly reduced to ~ 12 K, based on susceptibility measurements. The resonance in the neutron scattering measurements is also affected by the field. The resonance intensity under field cooling starts to rise at a lower temperature ~ 12 K, and the low temperature intensity is also reduced from the zero-field value. Our results provide clear evidence for the intimate relationship between superconductivity and the resonance measured in magnetic excitations of Fe-based superconductors.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
FeTe0.5Se0.5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	14	Pressure unresolved	onset
FeTe0.5Se0.5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	12	Pressure unresolved	zero_resistance
FeTe0.5Se0.5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	12	Pressure not reported	onset