Influence of aging on fishtail-effect in pure and Ag-doped MG-YBCO

D. Lotnyk; R. V. Vovk; M. A. Obolenskii; A. A. Zavgorodniy; J. Kovac; V. Antal; M. Kanuchova; M. Sefcikova; P. Diko; A. Feher

Influence of aging on fishtail-effect in pure and Ag-doped MG-YBCO

D. Lotnyk, R. V. Vovk, M. A. Obolenskii, A. A. Zavgorodniy, J. Kovac, V. Antal, M. Kanuchova, M. Sefcikova, P. Diko, A. Feher

arXiv:0911.3678 · 2009-11-18 · arXiv: Superconductivity

T1theoretical

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

$M(B)$-curves were experimentally investigated. Fishtail-effect (FE) was observed in MG YBa$_2$Cu$_3$O$_{7-δ}$ and YBa$_2$(Cu$_{1-x}$Ag$_x$)$_3$O$_{7-δ}$ (at $x \approx$ 0.02) crystals in a wide temperature range 0.4 $<T/T_c<$ 0.8 at the orientation of magnetic field $\textbf{H}\parallel c$. It was obtained that the influence of bulk pinning on FE is more effective at low temperatures while surface barriers dominates at high temperatures. The value $H_{max}$ for Ag-doped crystals is larger than for a pure one that due to the presence of additional pinning centers, above all on silver atoms.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
YBa2Cu3O7-δ Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	90.2	Pressure not reported	unknown
YBa2Cu3O7-δ Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	89.8	Pressure not reported	unknown
YBa2(Cu0.98Ag0.02)3O7-δ Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	91.3	Pressure not reported	unknown
YBa2(Cu0.98Ag0.02)3O7-δ Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	91.1	Pressure not reported	unknown