Nanostructural Superconducting Materials for Fault Current Limiters and Cryogenic Electrical Machines
T. A. Prikhna, W. Gawalek, Ya. M. Savchuk, N. V. Sergienko, V. E. Moshchil, V. Sokolovsky, J. Vajda, V. N. Tkach, F. Karau, H. Weber, M. Eisterer, A. Juolain, J. Rabier, X. Chaud, M. Wendt, J. Dellith, N. I. Danilenko, T. Habisreuther, S. N. Dub, V. Meerovich, D. Litzkendorf, P. A. Nagorny, L. K. Kovalev, Ch. Schmidt, V. S. Melnikov, A. P. Shapovalov, A. V. Kozyrev, V. B. Sverdun, J. Kosa, A. V. Vlasenko
arXiv:0912.4899 · DOI 10.12693/APHYSPOLA.117.7 · 2009-12-24 · Acta Physica Polonica A
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Materials of the Y-Ba-Cu-O (melt-textured YBa2Cu3O7-d-based materials or MT-YBCO) and Mg-B-O (MgB2-based materials) systems with high superconducting performance, which can be attained due to the formation of regularly distributed nanostructural defects and inhomogenities in their structure can be effectively used in cryogenic technique, in particular in fault current limiters and electrical machines (electromotors, generators, pumps for liquid gases, etc.). The developed processes of high-temperature (900-800 oC) oxygenation under elevated pressure (16 MPa) of MT-YBCO and high-pressure (2 GPa) synthesis of MgB2-based materials allowed us to attain high SC (critical current densities, upper critical fields, fields of irreversibility, trapped magnetic fields) and mechanical (hardness, fracture toughness, Young modulus) characteristics. It has been shown that the effect of materials properties improvement in the case of MT-YBCO was attained due to the formation of high twin density (20-22 micron-1), prevention of macrockracking and reduction (by a factor of 4.5) of microcrack density, and in the case of MgB2-based materials due to the formation of oxygen-enriched as compared to the matrix phase fine-dispersed Mg-B-O inhomogenities as well as inclusions of higher borides with near-MgB12 stoichiometry in the Mg-B-O matrix (with 15-37 nm average grain sizes). The possibility is shown to obtain the rather high Tc (37 K) and critical current densities in materials with MgB12 matrix (with 95 percent of shielding fraction as calculated from the resistant curve).
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB12 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 37 | Pressure not reported | unknown |
Similar papers
Higher borides and oxygen-enriched Mg-B-O inclusions as possible pinning centers in nanostructural magnesium diboride and the influence of additives on their formation
similarity 0.88Tatiana Prikhna et al. · 2010 · arXiv:1001.1904
Source status unknown — claims are unverified
High Critical Current Density and Improved Irreversibility Field in Bulk MgB2 Made By A Scaleable, Nanoparticle Addition Route
similarity 0.85J. Wang et al. · 2002 · arXiv:cond-mat/0204472
Source status unknown — claims are unverified
Superconducting Bulk Magnets: Very High Trapped Fields and Cracking
similarity 0.85S. Gruss et al. · 2001 · arXiv:cond-mat/0104396
Source status unknown — claims are unverified
Improved Irreversibility Behaviour and Critical Current Density in MgB2-Diamond Nanocomposites
similarity 0.84Y. Zhao et al. · 2003 · arXiv:cond-mat/0302365
Source status unknown — claims are unverified
MgB2 conductors for dc and ac applications
similarity 0.84B. A. Glowacki & M. Majoros · 2001 · arXiv:cond-mat/0109114
Source status unknown — claims are unverified
The Influence of Synthesis Parameters on Microstructures and Superconducting Properties of MgB2 Bulks
similarity 0.84Y. F. Wu et al. · 2006 · arXiv:cond-mat/0603536
Source status unknown — claims are unverified