Physical property characterization of single step synthesized NdFeAsO0.80F0.20 bulk 50K superconductor
V. P. S. Awana, R. S. Meena, Anand Pal, Arpita Vajpayee, K. V. R. Rao, H. Kishan
arXiv:1003.0273 · DOI 10.1140/epjb/e2010-10674-x · 2010-03-01 · The European Physical Journal B
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We report an easy single step synthesis route of title compound NdFeAsO0.80F0.20 superconductor having bulk superconductivity below 50 K. The title compound is synthesized via solid-state reaction route by encapsulation in an evacuated (10-3 Torr) quartz tube. Rietveld analysis of powder X-ray diffraction data shows that compound crystallized in tetragonal structure with space group P4/nmm. R(T)H measurements showed superconductivity with Tc (R=0) at 48 K and a very high upper critical field (Hc2) of up to 345 Tesla. Magnetic measurements exhibited bulk superconductivity in terms of diamagnetic onset below 50 K. The lower critical field (Hc1) is around 1000 Oe at 5 K. In normal state i.e., above 60 K, the compound exhibited purely paramagnetic behavior and thus ruling out the presence of any ordered FeOx impurity in the matrix. In specific heat measurements a jump is observed in the vicinity of superconducting transition (Tc) along with an upturn at below T=4 K due to the AFM ordering of Nd+3 ions in the system. The Thermo-electric power (TEP) is negative down to Tc, thus indicating dominant carriers to be of n-type in NdFeAsO0.80F0.20 superconductor. The granularity of the bulk superconducting NdFeAsO0.8F0.2 sample is investigated and the intra and inter grain contributions have been individuated by looking at various amplitude and frequencies of the applied AC drive magnetic field.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| NdFeAsO0.80F0.20 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 48 | Pressure not reported | zero_resistance |
| NdFeAsO0.80F0.20 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 50 | Pressure not reported | onset |
| NdFeAsO0.80F0.20 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
Very high critical field and superior Jc-field performance in NdO0.82F0.18FeAs with Tc of 51 K
similarity 0.89X. L. Wang et al. · 2008 · arXiv:0806.0063
Source status unknown — claims are unverified
Superconductivity in iron-based F-doped layered quaternary compound Nd[O1-xFx]FeAs
similarity 0.88Zhi-An Ren* et al. · 2008 · arXiv:0803.4234
Source status unknown — claims are unverified
Isovalent substitution effects of arsenic on structural and electrical properties of iron-based superconductor NdFeAsO0.8F0.2
similarity 0.88Z. Alborzi & V. Daadmehr · 2019 · arXiv:1901.00797
Source status unknown — claims are unverified
Superconductivity at high Tc in neodymium-doped 1111-SrFeAsF system
similarity 0.88S. V. Chong et al. · 2009 · arXiv:0908.3285
Source status unknown — claims are unverified
Influence of the Nd states on the magnetic behavior and the electric field gradient of the oxypnictides superconductors NdFeAsOF
similarity 0.87P. Jeglic et al. · 2009 · arXiv:0909.5335
Source status unknown — claims are unverified
Upper critical fields well above 100 T for the superconductor SmFeAsO0.85F0.15 with Tc=46 K
similarity 0.87C. Senatore et al.
Source status unknown — claims are unverified