Comparative study of transport and magnetic Jc in the polycrystalline iron-based superconductor NdFeAsO{0.88}F{0.12}

Y. Ding; Y. Sun; X. D. Wang; H. C. Wang; Z. X. Shi; Z. A. Ren; J. Yang; W. Lu

doi:10.1016/J.PHYSC.2010.09.012

← Back to search

Comparative study of transport and magnetic Jc in the polycrystalline iron-based superconductor NdFeAsO{0.88}F{0.12}

Y. Ding, Y. Sun, X. D. Wang, H. C. Wang, Z. X. Shi, Z. A. Ren, J. Yang, W. Lu

arXiv:1003.0946 · DOI 10.1016/J.PHYSC.2010.09.012 · 2010-03-04 · Physica C-superconductivity and Its Applications

T1experimental7 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Polycrystalline NdFeAsO0.88F0.12 superconductors prepared by high pressure (HP) and ambient pressure (AP) method were comparatively studied by magnetization and transport measurements. Upper critical field (Hc2), irreversibility field (Hirr) and the anisotropy parameter were estimated from resistance transition curves. The broadening of transition width was observed, and ascribed to both Hc2 anisotropy and superconductivity inhomogeneity of samples. Magnetic hysteresis loops (MHLs) in low fields were measured to detect the trace of weak-link behavior. The reclosed hysteresis loops in low fields manifest that there are weak-links in both samples. Magnetization critical current density Jcm were derived from MHLs. High-pressure synthesized sample shows higher Jcm. However, by means of direct transport I-V measurements, transport critical current density Jct was very low. The Jct values for two samples are comparable. Large discrepancies between Jcm and Jct also indicate that there are weak-links in both samples. The relative mechanism is discussed in detail.