Growth, Annealing Effects on Superconducting and Magnetic Properties and Anisotropy of FeSe_1-x_Te_x_ (0.5 =< x =< 1) Single Crystals
Takashi Noji, Takumi Suzuki, Haruki Abe, Tadashi Adachi, Masatsune Kato, Yoji Koike
arXiv:1004.1038 · 2010-04-07
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Single crystals of FeSe_1-x_Te_x_ (0.5=<x=<1) have been grown by the Bridgman method. After annealing them at 400 deg for 100 h in vacuum, single crystals of x=0.5-0.9 have exhibited bulk superconductivity. Anisotropic properties of the electrical resistivity and upper critical field, H_c2_, have been investigated for the single-crystal FeSe_1-x_Te_x_ with x=0.6. It has been found that the in-plane resistivity, Rho_ab_, shows a metallic temperature-dependence, while the out-of-plane resistivity, Rho_c_, shows a broad maximum around 100 K. The resistivity ratio, Rho_ab_/Rho_c_, is 44 and 70 at 290 K and just above the superconducting transition temperature, T_c_, respectively. The anisotropic parameter, gamma= H_c2_^para^/H_c2_^perp^ (The para and perp indicate field directions parallel and perpendicular to the ab-plane, respectively.), is estimated as 2.7 just below T_c_.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| FeSe0.4Te0.6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
Review of annealing effects and superconductivity in FeTeSe superconductors
similarity 0.92Yue Sun et al. · 2019 · arXiv:1908.09455
Source status unknown — claims are unverified
Anisotropic superconducting properties of single-crystalline FeSe0.5Te0.5
similarity 0.91M. Bendele et al.
Source status unknown — claims are unverified
Superconductivity, magnetism, and stoichiometry of single crystals of Fe1+y(Te1−xSx)z
similarity 0.91Rongwei Hu et al.
Source status unknown — claims are unverified
Evolution of superconducting and transport properties in annealed FeTeSe (0.1 0.4) multiband superconductors
similarity 0.90Yue Sun et al. · 2015 · arXiv:1502.04284
Source status unknown — claims are unverified
Transport properties and anisotropy of Rb0.8Fe2Se2 single crystals
similarity 0.90Chun-Hong Li et al. · 2010 · arXiv:1012.5637
Source status unknown — claims are unverified
Superconducting and tetragonal-to-orthorhombic transitions in single crystals of FeSe1−xTex (0≤ x ≤0.61)
similarity 0.90Kotaro Terao et al.
Source status unknown — claims are unverified