Heat treatment effects on the superconducting properties of Ag-doped SrKFeAs compound
Zhiyu Zhang, Lei Wang, Yanpeng Qi, Zhaoshun Gao, Dongliang Wang, Xianping Zhang, Yanwei Ma
arXiv:1004.2137 · 2010-04-13
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
The superconducting properties of polycrystalline Sr0.6K0.4Fe2As2 were strongly influenced by Ag doping (Supercond. Sci. Technol. 23 (2010) 025027). Ag addition is mainly dominated by silver diffusing, so the annealing process is one of the essential factors to achieve high quality Ag doped Sr0.6K0.4Fe2As2. In this paper, the optimal annealing conditions were studied for Ag doped Sr0.6K0.4Fe2As2 bulks prepared by a one-step solid reaction method. It is found that the annealing temperature has a strong influence on the superconducting properties, especially on the critical current density Jc. As a result, higher heat treatment temperature (~900C) is helpful in diffusing Ag and reducing the impurity phase gathered together to improve the grain connectivity. In contrast, low-temperature sintering is counterproductive for Ag doped samples. These results clearly suggest that annealing at ~900C is necessary for obtaining high Jc Ag-doped samples.
Similar papers
The role of silver addition on the structural and superconducting properties of polycrystalline Sr0.6K0.4Fe2As2
similarity 0.91Lei Wang et al. · 2009 · arXiv:0904.3145
Source status unknown — claims are unverified
Influence of Pb addition on the superconducting properties of polycrystalline Sr0.6K0.4Fe2As2
similarity 0.89Lei Wang et al. · 2010 · arXiv:1002.4305
Source status unknown — claims are unverified
Evolution of bulk superconductivity in SrFe2As2 with Ni substitution
similarity 0.88S. R. Saha et al.
Source status unknown — claims are unverified
The change of electronic state and crystal structure by post-annealing in superconducting SrFe2(As0.65P0.35)2
similarity 0.88T. Kobayashi et al. · 2013 · arXiv:1305.2074
Source status unknown — claims are unverified
Change of electronic state and crystal structure by postannealing in superconducting SrFe2(As0.65P0.35)2
similarity 0.87T. Kobayashi et al.
Source status unknown — claims are unverified
Enhanced critical current properties in Ba0.6K0.4+xFe2As2 superconductor by over-doping of potassium
similarity 0.87Chunlei Wang et al. · 2011 · arXiv:1101.5427
Source status unknown — claims are unverified