Intergrain effects in the AC susceptibility of polycrystalline LaFeAsO_{0.94}F_{0.06}: comparison with cuprate superconductors

G. Bonsignore; A. Agliolo Gallitto M. Li Vigni; J. L. Luo; G. F. Chen; N. L. Wang; D. V. Shovkun

Intergrain effects in the AC susceptibility of polycrystalline LaFeAsO_{0.94}F_{0.06}: comparison with cuprate superconductors

G. Bonsignore, A. Agliolo Gallitto M. Li Vigni, J. L. Luo, G. F. Chen, N. L. Wang, D. V. Shovkun

arXiv:1005.3965 · 2010-05-21

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

The AC susceptibility at zero DC magnetic field of a polycrystalline sample of LaFeAsO_{0.94}F_{0.06} (T_c = 24 K) has been investigated as a function of the temperature, the amplitude of the AC magnetic field (in the range Hac = 0.003 - 4 Oe) and the frequency (in the range f = 10 kHz - 100 kHz). The temperature dependence of the AC susceptibility exhibits the typical two-step transition arising from the combined response of superconduncting grains and intergranular weak-coupled medium. The intergranular part of the susceptibility strongly depends on both the amplitude and the frequency of the AC driving field, from few Kelvin below T_c down to T = 4.2 K. Our results show that, in the investigated sample, the intergrain critical current is not determined by pinning of Josephson vortices but by Josephson critical current across neighboring grains.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
LaFeAsO0.94F0.06 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	24	Pressure unresolved	unknown