Temperature-doping phase diagrams for Ba(Fe1-xTMx)2As2(TM=Ni, Cu, Cu / Co) single crystals
N. Ni, A. Thaler, J. Q. Yan, A. Kracher, E. Colombier, S. L. Bud'ko, P. C. Canfield
arXiv:1006.3193 · DOI 10.1103/PhysRevB.82.024519 · 2010-06-16 · Physical Review B
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Microscopic, structural, transport and thermodynamic measurements of single crystalline Ba(Fe1-xTMx)2As2 (TM = Ni and Cu) series, as well as two mixed TM = Cu / Co series, are reported. All the transport and thermodynamic measurements indicate that the structural and magnetic phase transitions at 134 K in pure BaFe2As2 are monotonically suppressed and increasingly separated in a similar manner by these dopants. In the Ba(Fe1-xNix)2As2 (x =< 0.072), superconductivity, with Tc up to 19 K, is stabilized for 0.024 =< x =< 0.072. In the Ba(Fe1-xCux)2As2 (x =< 0.356) series, although the structural and magnetic transitions are suppressed, there is only a very limited region of superconductivity: a sharp drop of the resistivity to zero near 2.1 K is found only for the x = 0.044 samples. In the Ba(Fe1-x-yCoxCuy)2As2 series, superconductivity, with Tc values up to 12 K (x ~ 0.022 series) and 20 K (x ~ 0.047 series), is stabilized. Quantitative analysis of the detailed temperature-dopant concentration (T-x) and temperature-extra electrons (T-e) phase diagrams of these series shows that there exists a limited range of the number of extra electrons added, inside which the superconductivity can be stabilized if the structural and magnetic phase transitions are suppressed enough. Moreover, comparison with pressure-temperature phase diagram data, for samples spanning the whole doping range, further reenforces the conclusion that suppression of the structural / magnetic phase transition temperature enhances Tc on the underdoped side, but for the overdoped side Tcmax is determined by e. Therefore, by choosing the combination of dopants that are used, we can adjust the relative positions of the upper phase lines (structural and magnetic phase transitions) and the superconducting dome to control the occurrence and disappearance of the superconductivity in transition metal, electron-doped BaFe2As2.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| Ba(Fe0.956Cu0.044)2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 2.1 | Pressure not reported | zero_resistance |
| Ba(Fe0.976Ni0.024)2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 8.6 | Pressure not reported | onset |
| Ba(Fe0.976Ni0.024)2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 6.8 | Pressure not reported | zero_resistance |
| Ba(Fe0.976Ni0.024)2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 3.9 | Pressure not reported | unknown |
| Ba(Fe0.976Ni0.024)2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 2.5 | Pressure not reported | unknown |
| Ba(Fe0.968Ni0.032)2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 16.6 | Pressure not reported | onset |
| Ba(Fe0.968Ni0.032)2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 15.9 | Pressure not reported | zero_resistance |
| Ba(Fe0.968Ni0.032)2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 15.1 | Pressure not reported | unknown |
| Ba(Fe0.968Ni0.032)2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 14.6 | Pressure not reported | unknown |
| Ba(Fe0.954Ni0.046)2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 19.4 | Pressure not reported | onset |
| Ba(Fe0.954Ni0.046)2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 18.8 | Pressure not reported | zero_resistance |
| Ba(Fe0.954Ni0.046)2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 18.4 | Pressure not reported | unknown |
| Ba(Fe0.954Ni0.046)2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 17.8 | Pressure not reported | unknown |
| Ba(Fe0.946Ni0.054)2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 15.5 | Pressure not reported | onset |
| Ba(Fe0.946Ni0.054)2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 14.3 | Pressure not reported | zero_resistance |
| Ba(Fe0.946Ni0.054)2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 14.4 | Pressure not reported | unknown |
| Ba(Fe0.946Ni0.054)2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 13.9 | Pressure not reported | unknown |
| Ba(Fe0.928Ni0.072)2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 7.5 | Pressure not reported | onset |
| Ba(Fe0.928Ni0.072)2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 5.7 | Pressure not reported | zero_resistance |
| Ba(Fe0.928Ni0.072)2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 6 | Pressure not reported | unknown |
| Ba(Fe0.928Ni0.072)2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 5.2 | Pressure not reported | unknown |
Similar papers
Microscopic coexistence of antiferromagnetic order and superconductivity in BaKFeAs
similarity 0.92Z. Li et al. · 2012 · arXiv:1204.2434
Source status unknown — claims are unverified
Character of the structural and magnetic phase transitions in the parent and electron doped BaFe2As2 compounds
similarity 0.92M. G. Kim et al. · 2011 · arXiv:1103.2752
Source status unknown — claims are unverified
Thermoelectric power of Ba(Fe1-xRux)2As2 and Ba(Fe1-xCox)2As2: possible changes of Fermi surface with and without changes in electron count
similarity 0.92H. Hodovanets et al. · 2010 · arXiv:1010.5111
Source status unknown — claims are unverified
Decoupling of the superconducting and magnetic (structural) phase transitions in electron-doped BaFe2As2
similarity 0.92P. C. Canfield et al. · 2009 · arXiv:0904.3134
Source status unknown — claims are unverified
Evolution of transport properties of BaFe2-xRuxAs2 in a wide range of isovalent Ru substitution
similarity 0.92M. J. Eom et al. · 2011 · arXiv:1109.1083
Source status unknown — claims are unverified
Abnormal T-linear susceptibility and Phase diagram of BaFeCoAs single crystals
similarity 0.92X. F. Wang et al. · 2008 · arXiv:0811.2920
Source status unknown — claims are unverified