Single crystal growth of BaFe$_{2-x}$Co$_x$As$_2$ without fluxing agent

Changjin Zhang; Lei Zhang; Chuanying Xi; Langsheng Ling; Shun Tan; Yuheng Zhang

Single crystal growth of BaFe$_{2-x}$Co$_x$As$_2$ without fluxing agent

Changjin Zhang, Lei Zhang, Chuanying Xi, Langsheng Ling, Shun Tan, Yuheng Zhang

arXiv:1011.0884 · 2010-11-03

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

We report a simple, reliable method to grow high quality BaFe$_{2-x}$Co$_x$As$_2$ single crystal samples without using any fluxing agent. The starting materials for the single crystal growth come from well-crystallized polycrystalline samples and the highest growing temperature can be 1493 K. The as-grown crystals have typical dimensions of 4$\times3\times$0.5 mm$^3$ with c-axis perpendicular to the shining surface. We find that the samples have very large current carrying ability, indicating that the samples have good potential technological applications.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
BaFe1.85Co0.15As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	23.3	Pressure not reported	zero_resistance
BaFe1.80Co0.20As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	23.1	Pressure not reported	unknown