Revised Phase Diagram for FeTe1-xSex system with less excess Fe atoms

Chihen Dong, Hangdong Wang, Zujuan Li, Jian Chen, H. Q. Yuan, Minghu Fang

arXiv:1012.5188 · DOI 10.1103/PhysRevB.84.224506 · 2010-12-23 · Physical Review B

T1theoretical82 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

We observed bulk superconductivity in the FeTe1-xSex crystals with a low Se concentration after the excess Fe atoms existing unavoidably in crystals as-grown are partially removed by means of annealing in the air. A revised magnetism and superconductivity phase diagram is obtained via resistivity and magnetic susceptibility measurements for FeTe1-xSex system. It is found that bulk superconductivity coexists with antiferromagnetic order in the crystals with 0.05<x<0.20. The phase diagram is very similar to the case of the K-doping or Co-doping BaFe2As2, as well as of SmFeAsO1-xFx iron-pnictide system, perhaps indicating that all iron-based systems have a generic phase diagram, although antiferromagnetic wave vector in the parent compounds of these systems is remarkable different.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
FeTe0.95Se0.05 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	6.7	Pressure unresolved	midpoint
FeTe0.93Se0.07 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	8.2	Pressure unresolved	midpoint
FeTe0.93Se0.07 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	4	Pressure unresolved	zero_resistance
FeTe0.90Se0.10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	9.6	Pressure unresolved	midpoint
FeTe0.90Se0.10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	7.6	Pressure unresolved	zero_resistance