Anisotropic magnetism, resistivity, London penetration depth and magneto-optical imaging of superconducting K0.80Fe1.76Se2 single crystals

R. Hu; K. Cho; H. Kim; H. Hodovanets; W. E. Straszheim; M. A. Tanatar; R. Prozorov; S. L. Bud'ko; P. C. Canfield

doi:10.1088/0953-2048/24/6/065006

← Back to search

Anisotropic magnetism, resistivity, London penetration depth and magneto-optical imaging of superconducting K0.80Fe1.76Se2 single crystals

R. Hu, K. Cho, H. Kim, H. Hodovanets, W. E. Straszheim, M. A. Tanatar, R. Prozorov, S. L. Bud'ko, P. C. Canfield

arXiv:1102.1931 · DOI 10.1088/0953-2048/24/6/065006 · 2011-02-09 · Superconductor Science and Technology

T1experimental17 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Single crystals of K0.80Fe1.76Se2.02 were suscessfully grown from a ternary solution. We show that although crystals form when cooling a near stoichiometric melt, crystals are actually growing out of a ternary solution that remains liquid to at least 850 C. We investigated their chemical composition, anisotropic magnetic susceptibility and resistivity, specific heat, thermoelectric power, London penetration depth and flux penetration via magneto-optical imaging. Whereas the samples appear to be homogeneously superconducting at low temperatures, there appears to be a broadened transtion range close to Tc ~ 30 K that may be associated with small variations in stociometry.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
K0.80Fe1.76Se2.02 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	30	Pressure not reported	unknown
K0.80Fe1.76Se2.02 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	30	Pressure not reported	unknown
K0.80Fe1.76Se2.02 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	30	Pressure not reported	unknown
K0.80Fe1.76Se2.02 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	30	Pressure not reported	unknown
K0.80Fe1.76Se2.02 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	30	Pressure not reported	unknown