Coexistence of superconductivity and antiferromagnetism in single crystals $A_{0.8}Fe_{2-y}Se_2$ (A= K, Rb, Cs, Tl/K and Tl/Rb): evidence from magnetization and resistivity

R. H. Liu; X. G. Luo; M. Zhang; A. F. Wang; J. J. Ying; X. F. Wang; Y. J. Yan; Z. J. Xiang; P. Cheng; G. J. Ye; Z. Y. Li; X. H. Chen

doi:10.1209/0295-5075/94/27008

Coexistence of superconductivity and antiferromagnetism in single crystals $A_{0.8}Fe_{2-y}Se_2$ (A= K, Rb, Cs, Tl/K and Tl/Rb): evidence from magnetization and resistivity

R. H. Liu, X. G. Luo, M. Zhang, A. F. Wang, J. J. Ying, X. F. Wang, Y. J. Yan, Z. J. Xiang, P. Cheng, G. J. Ye, Z. Y. Li, X. H. Chen

arXiv:1102.2783 · DOI 10.1209/0295-5075/94/27008 · 2011-02-14 · EPL (Europhysics Letters)

T1experimental89 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

We measure the resistivity and magnetic susceptibility in the temperature range from 5 K to 600 K for the single crystals $A$Fe$_{2-y}$Se$_2$ ($A$ = K$_{0.8}$, Rb$_{0.8}$, Cs$_{0.8}$, Tl$_{0.5}$K$_{0.3}$ and Tl$_{0.4}$Rb$_{0.4}$). A sharp superconducting transition is observed in low temperature resistivity and susceptibility, and susceptibility shows 100% Meissner volume fraction for all crystals, while an antiferromagnetic transition is observed in susceptibility at Neel temperature ($T_N$) as high as 500 K to 540 K depending on A. It indicates the coexistence of superconductivity and antiferromagnetism. A sharp increase in resistivity arises from the structural transition due to Fe vacancy ordering at the temperature slightly higher than $T_{\rm N}$. Occurrence of superconductivity in an antiferromagnetic ordered state with so high $T_{\rm N}$ may suggest new physics in this type of unconventional superconductors.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
K0.8Fe2-ySe2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	30	Pressure not reported	unknown
K0.8Fe2-ySe2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	30	Pressure not reported	unknown
Rb0.8Fe2-ySe2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	30	Pressure not reported	unknown
Rb0.8Fe2-ySe2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	30	Pressure not reported	unknown
Cs0.8Fe2-ySe2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	30	Pressure not reported	unknown
Cs0.8Fe2-ySe2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	30	Pressure not reported	unknown
Tl0.5K0.3Fe2-ySe2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	30	Pressure not reported	unknown
Tl0.5K0.3Fe2-ySe2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	30	Pressure not reported	unknown
Tl0.4Rb0.4Fe2-ySe2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	30	Pressure not reported	unknown
Tl0.4Rb0.4Fe2-ySe2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	30	Pressure not reported	unknown
Cs0.8(FeSe0.98)2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	28	Pressure not reported	unknown