Doping dependent evolution of magnetism and superconductivity in Eu1-xKxFe2As2 (x = 0-1) and temperature dependence of lower critical field Hc1

Abstract

We have synthesized the polycrystalline samples of Eu1-xKxFe2As2 (x = 0-1) and carried out systematic characterization using x-ray diffraction, ac & dc magnetic susceptibility, and electrical resistivity measurements. We have seen a clear signature of the coexistence of superconducting transition (Tc = 5.5 K) with SDW ordering in our under doped sample viz. x = 0.15. The spin density wave transition observed in EuFe2As2 get completely suppressed at x = 0.3 and superconductivity arises below 20 K. Superconducting transition temperature Tc increases with increase in K content and a maximum Tc = 33 K is reached for x = 0.5, beyond which it decreases again. The doping dependent T(x) phase diagram is extracted from the magnetic and electrical transport data. It is found that magnetic ordering of Eu-moments coexists with superconductivity up to x = 0.6. The isothermal magnetization data taken at 2 K for the doped samples suggest 2+ valence states of Eu ions. We also present the temperature dependence of the lower critical field Hc1 of superconducting polycrystalline samples. The value of Hc1(0) obtained for x = 0.3, 0.5, and 0.7 after taking the demagnetization factor into account is 248, 385, and 250 Oe, respectively. The London penetration depth λ(T) calculated from the lower critical field does not show exponential behaviour at low temperature, as would be expected for a fully gapped clean s-wave superconductor. In contrast, it shows a T2 power-law feature down to T = 0.4 Tc, as observed in Ba1-xKxFe2As2 and BaFe2-xCoxAs2.

Source-reported materials — not catalogue approval

Similar papers