T. Nakano; N. Fujiwara; S. Tsutsumi; H. Ogino; K. Kishio; J. Shimoyama

doi:10.1103/PhysRevB.84.060502

← Back to search

Successive transition from superconducting to antiferromagnetic phase in (Ca_6(Al, Ti)_4O_y)Fe_2As_2 studied via ^{75}As and ^{27}Al NMR

T. Nakano, N. Fujiwara, S. Tsutsumi, H. Ogino, K. Kishio, J. Shimoyama

arXiv:1107.2765 · DOI 10.1103/PhysRevB.84.060502 · 2011-07-14 · Physical Review B

T1theoretical3 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

An unusual successive phase transition from superconducting (SC) to antiferromagnetic (AF) phases was discovered via ^{75}As and ^{27}Al nuclear magnetic resonance (NMR) in (Fe_2As_2)(Ca_6(Al, Ti)_4O_y) with four (Al, Ti)O layers intercalated between FeAs planes. Although the spatially-uniform AF ordering is clearly visible from ^{27}Al spectra, the ordered moments are very small and the low-frequency fluctuation is much suppressed, contrary to existing pnictides with localized magnetic elements. Furthermore, the temperature (T) dependence of the fluctuation at both nuclei is very similar throughout the entire temperature range. These facts suggest that some hybridization between Ti and Fe orbitals induces a uniform electronic state within FeAs and (Al, Ti)O layers accompanied by the SC and AF transitions. The iron-based pnictide with Ti-doped blocking layers is the first high-T_c compound having metallic blocking layers.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
(Fe2As2)(Ca6(Al,Ti)4Oy) Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	39	Pressure not reported	onset
(Fe2As2)(Ca6(Al,Ti)4Oy) Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	30	Pressure not reported	zero_resistance
(Fe2As2)(Ca6(Al,Ti)4Oy) Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	30	Pressure not reported	unknown
(Fe2As2)(Ca6(Al,Ti)4Oy) Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	23	Pressure not reported	unknown
(Fe2As2)(Ca4(Mg,Ti)3Oy) Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	47	Pressure not reported	unknown
(Fe2As2)(Ca5(Sc,Ti)4Oy) Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
(Fe2As2)(Ca6(Sc,Ti)5Oy) Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
(Fe2As2)(Sr4(Mg,Ti)2O6) Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	35	Pressure not reported	unknown
(Fe2As2)(Sr4V2O6) Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	37	Pressure not reported	unknown