Interplay of composition, structure, magnetism, and superconductivity in SmFeAs1-xPxO1-y
N. D. Zhigadlo, S. Katrych, M. Bendele, P. J. W. Moll, M. Tortello, S. Weyeneth, V. Yu. Pomjakushin, J. Kanter, R. Puzniak, Z. Bukowski, H. Keller, R. S. Gonnelli, R. Khasanov, J. Karpinski, B. Batlogg
arXiv:1107.5715 · 2011-07-28
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Polycrystalline samples and single crystals of SmFeAs1-xPxO1-y were synthesized and grown employing different synthesis methods and annealing conditions. Depending on the phosphorus and oxygen content, the samples are either magnetic or superconducting. In the fully oxygenated compounds the main impact of phosphorus substitution is to suppress the Néel temperature TN of the spin density wave (SDW) state, and to strongly reduce the local magnetic field in the SDW state, as deduced from muon spin rotation measurements. On the other hand the superconducting state is observed in the oxygen deficient samples only after heat treatment under high pressure. Oxygen deficiency as a result of synthesis at high pressure brings the Sm-O layer closer to the superconducting As/P-Fe-As/P block and provides additional electron transfer. Interestingly, the structural modifications in response to this variation of the electron count are significantly different when phosphorus is partly substituting arsenic. Point contact spectra are well described with two superconducting gaps. Magnetic and resistance measurements on single crystals indicate an in-plane magnetic penetration depth of 200 nm and an anisotropy of the upper critical field slope of 4-5. PACS number(s): 74.70.Xa, 74.62.Bf, 74.25.-q, 81.20.-n
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| SmFeAs1-xPxO1-y Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | — |
| SmFeAs1-xPxO1-y Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | — |
| SmFeAs1-xPxO1-y Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | — |
Similar papers
Interplay of composition, structure, magnetism, and superconductivity in SmFeAs1−xPxO1−y
similarity 0.99N. D. Zhigadlo et al.
Source status unknown — claims are unverified
Magnetic properties of undoped and 15%F doped SmFeAsO compounds
similarity 0.89R. Cimberle et al. · 2008 · arXiv:0807.1688
Source status unknown — claims are unverified
High- Iron-phosphide Superconductivity Enhanced by Reemergent Antiferromagnetic Spin Fluctuations in (SrScO)Fe(AsP) probed by NMR
similarity 0.87F. Sakano et al. · 2019 · arXiv:1908.02980
Source status unknown — claims are unverified
Optical investigations of the chemical pressurized EuFe2(As1-xPx)2: an s-wave superconductor with strong interband interaction
similarity 0.87D. Wu et al. · 2010 · arXiv:1011.1207
Source status unknown — claims are unverified
Interplay of antiferromagnetism, ferromagnetism and superconductivity in EuFe_2(As_1-xP_x)_2 single crystals
similarity 0.87H. S. Jeevan et al. · 2010 · arXiv:1011.4481
Source status unknown — claims are unverified
Muon spin rotation study of magnetism and superconductivity in BaFe2-xCoxAs2 and Pr1-xSrxFeAsO
similarity 0.87C. Bernhard et al. · 2009 · arXiv:0902.0859
Source status unknown — claims are unverified