Combined effects of pressure and Ru substitution on BaFe2As2

S. K. Kim; M. S. Torikachvili; E. Colombier; A. Thaler; S. L. Bud'ko; P. C. Canfield

doi:10.1103/PhysRevB.84.134525

← Back to search

Combined effects of pressure and Ru substitution on BaFe2As2

S. K. Kim, M. S. Torikachvili, E. Colombier, A. Thaler, S. L. Bud'ko, P. C. Canfield

arXiv:1107.6034 · DOI 10.1103/PhysRevB.84.134525 · 2011-07-29 · Physical Review B

T1theoretical38 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

The ab-plane resistivity of Ba(Fe1-xRux)2As2 (x = 0.00, 0.09, 0.16, 0.21, and 0.28) was studied under nearly hydrostatic pressures, up to 7.4 GPa, in order to explore the T-P phase diagram and to compare the combined effects of iso-electronic Ru substitution and pressure. The parent compound BaFe2As2 exhibits a structural/magnetic phase transition near 134 K. At ambient pressure, progressively increasing Ru concentration suppresses this phase transition to lower temperatures at the approximate rate of ~5 K/% Ru and is correlated with the emergence of superconductivity. By applying pressure to this system, a similar behavior is seen for each concentration: the structural/magnetic phase transition is further suppressed and superconductivity induced and ultimately, for larger x Ru and P, suppressed. A detailed comparison of the T-P phase diagrams for all Ru concentrations shows that 3 GPa of pressure is roughly equivalent to 10% Ru substitution. Furthermore, due to the sensitivity of Ba(Fe1-xRux)2As2 to pressure conditions, the melting of the liquid media, 4 : 6 light mineral oil : n-pentane and 1 : 1 iso-pentane : n-pentane, used in this study could be readily seen in the resistivity measurements. This feature was used to determine the freezing curves for these media and infer their room temperature, hydrostatic limits: 3.5 and 6.5 GPa, respectively.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
Ba(Fe0.72Ru0.28)2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	16	Pressure unresolved	onset
Ba(Fe0.79Ru0.21)2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	20.3	2.27 GPa	zero_resistance
Ba(Fe0.84Ru0.16)2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	23	3.57 GPa	zero_resistance
Ba(Fe0.84Ru0.16)2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	22.9	4.09 GPa	zero_resistance
Ba(Fe0.91Ru0.09)2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	25.7	4.94 GPa	zero_resistance