Anisotropy in BaFe2Se3 single crystals with double chains of FeSe tetrahedra

Hechang Lei; Hyejin Ryu; Anatoly Frenkel; C. Petrovic

Anisotropy in BaFe2Se3 single crystals with double chains of FeSe tetrahedra

Hechang Lei, Hyejin Ryu, Anatoly Frenkel, C. Petrovic

arXiv:1110.3039 · 2011-10-13

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

We studied the anisotropy in physical properties of Ba1.00(4)Fe1.9(1)Se3.1(1) single crystals. BaFe2Se3 is a semiconductor below 300 K. Magnetization measurements show that there is a crossover from short-range antiferromagnetic (AFM) correlations at room temperature to a long-range AFM order with TN = 255 K. The anisotropy of magnetization is consistent with the previous neutron results. This crossover is supported by the heat-capacity measurement, where the phase-transition peak is absent at 255 K. The superconducting transition at about 10 K is likely due to the small amount of beta-FeSe impurities.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	10	Pressure not reported	unknown
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	8.5	Pressure not reported	unknown
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	36.7	8.9 GPa	unknown