Residual Strain Dependence on Matrix Structure in RHQ-Nb3Al Wires by Neutron Diffraction Measurement
Xinzhe Jin, Tatsushi Nakamoto, Takayoshi Ito, Stefanus Harjo, Akihiro Kikuchi, Takao Takeuchi, Kiyosumi Tsuchiya, Tsutomu Hemmi, Toru Ogitsu, Akira Yamamoto
arXiv:1111.0747 · DOI 10.1088/0953-2048/25/6/065021 · 2011-11-03 · Superconductor Science and Technology
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We prepared three types of non-Cu RHQ-Nb3Al wire samples with different matrix structures: an all-Ta matrix,a composite matrix of Nb and Ta with a Ta inter filament, and an all-Nb matrix. Neutron diffraction patterns of the wire samples were measured at room temperature in J-PARC "TAKUMI". To obtain residual strains of materials, we estimated lattice constant a by multi-peak analysis in the wire. Powder sample of each wire was measured, where the powder was considered to be strain-free. The grain size of all the powder samples was below 0.02 mm. For wire sample with the all-Nb matrix, we also obtained lattice spacing d by a single-peak analysis. Residual strains of Nb3Al filament were estimated from the two analysis results and were compared. Result, residual strains obtained from the multi-peak analysis showed a good accuracy with small standard deviation. The multi-peak analysis results for the residual strains of Nb3Al filament in the three samples were all tensile residual strain in the axial direction, they are 0.12%, 0.12%, and 0.05% for the all-Ta matrix, the composite matrix, and the all-Nb matrix, respectively. Difference in the residual strain of Nb3Al filament between the composite and all-Nb matrix samples indicates that type of inter-filament materials show a great effect on the residual strain. In this paper, we report the method of measurement, method of analysis, and results for residual strain in the tree types of non-Cu RHO-Nb3Al wires.
Similar papers
Influence of Nb Alloying on Nb Recrystallization and the Upper Critical Field of Nb3Sn
similarity 0.85Nawaraj Paudel et al. · 2024 · arXiv:2412.09514
Source status unknown — claims are unverified
Antiferromagnetic spin fluctuations and superconductivity in NbRhB and TaRhB with a chiral crystal structure
similarity 0.84Kazuaki Matano et al. · 2021 · arXiv:2110.04958
Source status unknown — claims are unverified
High Critical Temperature and Field Superconductivity in NbX, (X = Ti, Zr, Hf) Alloys: Promising Candidates for Superconducting Devices
similarity 0.83R. K. Kushwaha et al. · 2025 · arXiv:2512.18821
Source status unknown — claims are unverified
A review and prospects for Nb3Sn superconductor development
similarity 0.83Xingchen Xu · 2017 · arXiv:1706.10253
Source status unknown — claims are unverified
Metallurgy, superconductivity, and hardness of a new high-entropy alloy superconductor Ti-Hf-Nb-Ta-Re
similarity 0.82Takuma Hattori et al. · 2023 · arXiv:2307.01958
Source status unknown — claims are unverified
Doping evolution of antiferromagnetism and transport properties in the non-superconducting BaFe2-2xNixCrxAs2
similarity 0.82Rui Zhang et al. · 2015 · arXiv:1502.07950
Source status unknown — claims are unverified