Anuj Kumar, Rajveer Jha, R. P. Tandon, V. P. S. Awana
arXiv:1204.6175 · DOI 10.1016/j.ssc.2012.04.077 · 2012-04-27 · Solid State Communications
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We report synthesis, structural and magnetic (DC and AC) properties of Boron substituted MgCNi3 superconductor. A series of polycrystalline bulk samples Mg1.2C1.6-xBxNi3 (x = 0.0, 0.08 and 0.16) is synthesized through standard solid-state reaction route, which are found to crystallize in cubic perovskite structure with space group Pm3m. Rietveld analysis of observed XRD data show that lattice parameters expand from a = 3.8106 (4) Å for pure, to 3.8164 (2) Å and 3.8173 (5) Å for 5% and 10% Boron substituted samples respectively. DC magnetization exhibited superconducting transition (Tc) at around 7.3 K for pure sample, and the same decreases slightly with Boron substitution. The lower critical field (Hc1) at 2 K is around 150 Oe for pure sample, which increases slightly with Boron substitution. For pure sample the upper critical field (Hc2) being determined from AC susceptibility measurements is 11.6 kOe and 91.70 kOe with 50% and 90% diamagnetism criteria respectively, which decreases to 5.57 kOe and 42.5 kOe respectively for 10% Boron substituted sample. 10% Boron substitution at Carbon site has decreased both the Hc2 and Tc. On the other hand lower critical field (Hc1) at 2 K is slightly increased from around 150 Oe for pure sample, to 200 Oe for 10% Boron substituted sample. Seemingly, the Carbon site Boron substitution induced disorder though has increased slightly the Hc1 but with simultaneous decrease in superconducting transition temperature (Tc) and upper critical field (Hc2). The high relative proportion of Ni in studied MgCNi3 suggests that magnetic interactions are important and non-oxide perovskite structure make it interesting.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| Mg1.2C1.6Ni3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 7.3 | Pressure not reported | unknown |
| Mg1.2C1.6Ni3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | — |
| Mg1.2C1.44B0.16Ni3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | — |
Similar papers
Superconductivity in the vicinity of ferromagnetism in oxygen free perovskite MgCNi3: An experimental and DFT (Density Functional Theory) study
similarity 0.93Anuj Kumar et al. · 2011 · arXiv:1105.0482
Source status unknown — claims are unverified
The suppression of superconductivity in MgCNi3 by Ni-site doping
similarity 0.91M. A. Hayward et al. · 2001 · arXiv:cond-mat/0104541
Source status unknown — claims are unverified
The effect of {11}^B substitution on the superconductivity in MgCNi3
similarity 0.91T. Klimczuk et al. · 2004 · arXiv:cond-mat/0412551
Source status unknown — claims are unverified
Carbon Concentration Dependence of the Superconducting Transition Temperature and Structure of MgCxNi3
similarity 0.90T. G. Amos et al. · 2001 · arXiv:cond-mat/0110604
Source status unknown — claims are unverified
Electronic structures of antiperovskite superconductors: MgXNi (X=B,C,N)
similarity 0.90J. H. Shim & B. I. Min · 2001 · arXiv:cond-mat/0105418
Source status unknown — claims are unverified
Study of Normal and Superconducting States of MgCNi_3 upon Fe and Co Substitution and External Pressure
similarity 0.90T. Geetha Kumary et al. · 2002 · arXiv:cond-mat/0202277
Source status unknown — claims are unverified