Effect of Ni-doping on magnetism and superconductivity in Eu0.5K0.5Fe2As2

Anupam; V. K. Anand; P. L. Paulose; S. Ramakrishnan; C. Geibel; Z. Hossain

doi:10.1103/PhysRevB.85.144513

← Back to search

Effect of Ni-doping on magnetism and superconductivity in Eu0.5K0.5Fe2As2

Anupam, V. K. Anand, P. L. Paulose, S. Ramakrishnan, C. Geibel, Z. Hossain

arXiv:1208.0929 · DOI 10.1103/PhysRevB.85.144513 · 2012-08-04 · Physical Review B

T1theoretical9 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

The effect of Ni-doping on the magnetism and superconductivity in Eu0.5K0.5Fe2As2 has been studied through a systematic investigation of magnetic and superconducting properties of Eu0.5K0.5(Fe1-xNix)2As2 (x = 0, 0.03, 0.05, 0.08 and 0.12) compounds by means of dc and ac magnetic susceptibilities, electrical resistivity and specific heat measurements. Eu0.5K0.5Fe2As2 is known to exhibit superconductivity with superconducting transition temperature Tc as high as 33 K. The Ni-doping leads to a rapid decrease in Tc; Tc is reduced to 23 K with 3% Ni-doping, and 8% Ni-doping suppresses the superconductivity to below 1.8 K. In 3% Ni-doped sample Eu0.5K0.5(Fe0.97Ni0.03)2As2 superconductivity coexists with short range ordering of Eu2+ magnetic moments at Tm ~ 6 K. The suppression of superconductivity with Ni-doping is accompanied with the emergence of a long range antiferromagnetic ordering with TN = 8.5 K and 7 K for Eu0.5K0.5(Fe0.92Ni0.08)2As2 and Eu0.5K0.5(Fe0.88Ni0.12)2As2, respectively. The temperature and field dependent magnetic measurements for x = 0.08 and 0.12 samples reflect the possibility of a helical magnetic ordering of Eu2 moments. We suspect that the helimagnetism of Eu spins could be responsible for the destruction of superconductivity as has been observed in Co-doped EuFe2As2. The most striking feature seen in the resistivity data for x = 0.08 is the reappearance of the anomaly presumably due to spin density wave transition at around 60 K. This could be attributed to the compensation of holes (K-doping at Eu-site) by the electrons (Ni-doping at Fe site). The anomaly associated with spin density wave further shifts to 200 K for x = 0.12 for which the electron doping has almost compensated the holes in the system.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
Eu0.5K0.5Fe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	33	Pressure unresolved	unknown
Eu0.5K0.5(Fe0.97Ni0.03)2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	23	Pressure unresolved	onset
Eu0.5K0.5(Fe0.95Ni0.05)2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	18	Pressure unresolved	onset
Eu0.5K0.5(Fe0.92Ni0.08)2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure unresolved	unknown
Eu0.5K0.5(Fe0.88Ni0.12)2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure unresolved	unknown