Superconductivity at 5K in NdO0.5F0.5BiS2

Rajveer Jha; Anuj Kumar; Shiva Kumar Singh; V. P. S. Awana

doi:10.1063/1.4790322

← Back to search

Superconductivity at 5K in NdO0.5F0.5BiS2

Rajveer Jha, Anuj Kumar, Shiva Kumar Singh, V. P. S. Awana

arXiv:1208.3077 · DOI 10.1063/1.4790322 · 2012-08-15 · arXiv: Superconductivity

T1experimental80 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

We report appearance of superconductivity at 5K in NdO0.5F0.5BiS2 and supplement the discovery [1] of the same in layered sulfide based ZrCuSiAs type compounds. The bulk polycrystalline compound is synthesized by conventional solid state route via vacuum encapsulation technique. Detailed structural analysis showed that the studied compound is crystallized in tetragonal P4/nmm space group with lattice parameters a = 3.9911(3) Å, c = 13.3830(2) Å. Bulk superconductivity is established in NdO0.5F0.5BiS2 at 5K by both transport and magnetic measurements. Electrical transport measurements showed superconducting Tc onset at 5.2K and Tc (ρ=0) at 4.7K. Under applied magnetic field both Tc onset and Tc (ρ =0) decrease to lower temperatures and an upper critical field [Hc2(0)] of above 23kOe is estimated. Both AC and DC magnetic susceptibility measurements showed bulk superconductivity below 5K. Isothermal magnetization (MH) exhibited typical type II behavior with lower critical field (Hc1) of around 15Oe. Isothermal magnetization (MH) exhibited typical type-II behavior with lower critical field (Hc1) of around 15Oe. Specific heat [Cp(T)] is investigated in the temperature range of 1.9-50K in zero external magnetic field. A Schottky-type anomaly is observed at low temperature below 7K. This low temperature Schottky can be attributed to the change in the entropy of the system.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
NdO0.5F0.5BiS2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	5.2	Pressure not reported	onset
NdO0.5F0.5BiS2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	4.7	Pressure not reported	zero_resistance
NdO0.5F0.5BiS2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	5	Pressure not reported	unknown