P. Dhakal, G. Ciovati, G. R. Myneni, K. E. Gray, N. Groll, P. Maheshwari, D. M. McRae, R. Pike, T. Proslier, F. Stevie, R. P. Walsh, Q. Yang, J. Zasadzinzki
arXiv:1210.6875 · DOI 10.1103/PhysRevSTAB.16.042001 · 2012-10-25 · Physical Review Special Topics-accelerators and Beams
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Large-grain Nb has become a viable alternative to fine-grain Nb for the fabrication of superconducting radio-frequency cavities. In this contribution we report the results from a heat treatment study of a large-grain 1.5 GHz single-cell cavity made of "medium purity" Nb. The baseline surface preparation prior to heat treatment consisted of standard buffered chemical polishing. The heat treatment in the range 800 - 1400 C was done in a newly designed vacuum induction furnace. Q0 values of the order of 2x1010 at 2.0 K and peak surface magnetic field (Bp) of 90 mT were achieved reproducibly. A Q0-value of (5+-1)1010 at 2.0 K and Bp = 90 mT was obtained after heat treatment at 1400 C. This is the highest value ever reported at this temperature, frequency and field. Samples heat treated with the cavity at 1400 C were analyzed by secondary ion mass spectrometry, secondary electron microscopy, energy dispersive X-ray, point contact tunneling and X-ray diffraction and revealed a complex surface composition which includes titanium oxide, increased carbon and nitrogen content but reduced hydrogen concentration compared to a non heat-treated sample.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| Nb Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
Effect of high temperature heat treatments on the quality factor of a large-grain superconducting radio-frequency niobium cavity
similarity 0.90P. Dhakal et al.
Source status unknown — claims are unverified
Determination of the BCS material parameters of the HIE-ISOLDE superconducting resonator
similarity 0.88A. Miyazaki & W. Venturini Delsolaro · 2018 · arXiv:1806.04443
Source status unknown — claims are unverified
Effect of low temperature baking in nitrogen on the performance of a niobium superconducting radio frequency cavity
similarity 0.87Pashupati Dhakal et al.
Source status unknown — claims are unverified
Ac losses in field-cooled type I superconducting cavities
similarity 0.87G. Catelani et al. · 2021 · arXiv:2110.02866
Source status unknown — claims are unverified
Smooth, homogeneous, high-purity Nb3Sn superconducting RF resonant cavity by seed-free electrochemical synthesis
similarity 0.87Zeming Sun et al. · 2023 · arXiv:2302.02054
Source status unknown — claims are unverified
Resonance Frequency Shift Measurements of SRF Cavities at DESY
similarity 0.87Rezvan Ghanbari et al. · 2026 · arXiv:2604.22596
Source status unknown — claims are unverified