MOD derived pyrochlore films as buffer layer for all-chemical YBCO coated conductors
Andrea Augieri, Angelo Vannozzi, Rita Mancini, Achille Armenio Angrisani, Fabio Fabbri, Valentina Galluzzi, Alessandro Rufoloni, Francesco Rizzo, Antonella Mancini, Giuseppe Celentano, Ivan Colantoni, Ivan Davoli, Nicola Pompeo, Giovanni Sotgiu, Enrico Silva
arXiv:1210.8289 · DOI 10.1109/TASC.2012.2234175 · 2012-10-31 · IEEE Transactions on Applied Superconductivity
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We report a detailed study performed on La2Zr2O7 (LZO) pyrochlore material grown by Metal-Organic Decomposition (MOD) method as buffer layers for YBa2Cu3O7-x (YBCO) coated conductors. High quality epitaxial LZO thin films have been obtained on single crystal (SC) and Ni-5%at.W substrates. In order to evaluate structural and morphological properties, films have been characterized by means of X-ray diffraction analyses (XRD), atomic force microscope (AFM) and scanning electron microscope (SEM). Precursors solutions and heat treatments have been studied by thermogravimetric analyses (TG-DTA-DTG) and infrared spectra (FT-IR) with the aim of optimizing the annealing process. Thin films of YBCO have been deposited by pulsed laser ablation (PLD) on this buffer layers. The best results obtained on SC showed YBCO films with critical temperature values above 90 K, high self field critical current density values (Jc > 1 MA/cm2) and high irreversibility field values (8.3 T) at 77 K together with a rather high depinning frequency vp (0.5 T, 77 K)>44 GHz as determined at microwaves. The best results on Ni-5%at.W has been obtained introducing in the heat treatment a pyrolysis process at low temperature in air in order to remove the residual organic part of the precursor solution.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| YBa2Cu3O7-x Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 90 | Pressure not reported | unknown |
Similar papers
buffer layers on inclined substrate deposited MgO templates for coated conductors
similarity 0.86Oleksiy Troshyn et al. · 2020 · arXiv:2012.01318
Source status unknown — claims are unverified
Strong Reduction of the Field-Dependent Microwave Surface Resistance in YBCO with BaZrO_3 Inclusions
similarity 0.84N. Pompeo et al. · 2007 · arXiv:0710.1953
Source status unknown — claims are unverified
Superconductivity of one-unit-cell thick YBa2Cu3O7 thin film
similarity 0.84T. Terashima et al.
Source status unknown — claims are unverified
Fast track to the overdoped regime of superconducting YBa2Cu3O7-δ thin films via electrochemical oxidation
similarity 0.84Alexander Stangl et al. · 2025 · arXiv:2512.01146
Source status unknown — claims are unverified
Through-thickness superconducting and normal-state transport properties revealed by thinning of thick film ex situ YBa2Cu3O7-x coated conductors
similarity 0.83D. M. Feldmann et al. · 2003 · arXiv:cond-mat/0310123
Source status unknown — claims are unverified
Transport properties of ultrathin YBaCuO nanowires: a route to single photon detection
similarity 0.83Riccardo Arpaia et al. · 2017 · arXiv:1708.04721
Source status unknown — claims are unverified