Superconducting Phases in Potassium-Intercalated Iron Selenides

Tianping Ying; Xiaolong Chen; Gang Wang; Shifeng Jin; Xiaofang Lai; Tingting Zhou; Han Zhang; Shijie Shen; Wanyan Wang

doi:10.1021/ja312705x

← Back to search

Superconducting Phases in Potassium-Intercalated Iron Selenides

Tianping Ying, Xiaolong Chen, Gang Wang, Shifeng Jin, Xiaofang Lai, Tingting Zhou, Han Zhang, Shijie Shen, Wanyan Wang

arXiv:1302.7178 · DOI 10.1021/ja312705x · 2013-02-28 · Journal of the American Chemical Society

T1experimental149 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

The ubiquitous coexistence of majority insulating 245 phases and minority superconducting (SC) phases in AxFe2-ySe2 (A = K, Cs, Rb, Tl/Rb, Tl/K) formed by high-temperature routes makes pure SC phases highly desirable for studying the intrinsic properties of this SC family. Here we report that there are at least two pure SC phases, KxFe2Se2(NH3)y (x ~ 0.3 and 0.6), determined mainly by potassium concentration in the K-intercalated iron selenides formed via the liquid ammonia route. K0.3Fe2Se2(NH3)0.47 corresponds to the 44 K phase with lattice constant c = 15.56(1) angstroms and K0.6Fe2Se2(NH3)0.37 to the 30 K phase with c = 14.84(1) angstroms. With higher potassium doping, the 44 K phase can be converted into the 30 K phase. NH3 has little, if any, effect on superconductivity. Thus, the conclusions should apply to both K0.3Fe2Se2 and K0.6Fe2Se2 SC phases. K0.3Fe2Se2(NH3)0.47 and K0.6Fe2Se2(NH3)0.37 stand out among known superconductors as their structures are stable only at particular potassium doping levels, and hence the variation of Tc with doping is not dome-like.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
K0.3Fe2Se2(NH3)0.47 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	44	Pressure not reported	unknown
K0.6Fe2Se2(NH3)0.37 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	30	Pressure not reported	unknown
K0.3Fe2Se2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	44	Pressure not reported	unknown
K0.6Fe2Se2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	30	Pressure not reported	unknown