Large, Homogeneous, and Isotropic Critical Current Density in Oxygen-Annealed Fe1+yTe0.6Se0.4 Single Crystal

Yue Sun; Toshihiro Taen; Yuji Tsuchiya; Qingping Ding; Sunsen Pyon; Zhixiang Shi; Tsuyoshi Tamegai

doi:10.7567/APEX.6.043101

← Back to search

Large, Homogeneous, and Isotropic Critical Current Density in Oxygen-Annealed Fe1+yTe0.6Se0.4 Single Crystal

Yue Sun, Toshihiro Taen, Yuji Tsuchiya, Qingping Ding, Sunsen Pyon, Zhixiang Shi, Tsuyoshi Tamegai

arXiv:1304.1617 · DOI 10.7567/APEX.6.043101 · 2013-04-05 · Applied Physics Express

T1theoretical29 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

We reported a controllable way of removing excess Fe in Fe1+yTe0.6Se0.4 by annealing in a fixed amount of O2. Compared with the weak superconductivity induced by dilute acids, O2 annealing can successfully induce bulk superconductivity. Proper O2 annealing changes the temperature dependence of resistivity at low temperatures from semiconducting to metallic, which comes from the deintercalation of excess Fe. Critical current densities with field along the c-axis and ab-plane are found almost isotropic with large values of 3*10^5 A/cm2 and 2.5*10^5 A/cm2 at 2 K. Furthermore, magneto-optical images reveal isotropic current flow within the ab-plane.