Electrical and Magnetic behaviour of PrFeAsO0.8F0.2 superconductor

R S Meena; Anand Pal; K V R Rao; Hari Kishan; V. P. S. Awana

← Back to search

Electrical and Magnetic behaviour of PrFeAsO0.8F0.2 superconductor

R S Meena, Anand Pal, K V R Rao, Hari Kishan, V. P. S. Awana

arXiv:1308.3557 · 2013-08-16 · arXiv: Superconductivity

T1theoretical2 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

The superconducting and ground state samples of PrFeAsO0.8F0.2 and PrFeAsO have been synthesised via easy and versatile single step solid state reaction route. X-ray & Reitveld refine parameters of the synthesised samples are in good agreement to the earlier reported value of the structure. The ground state of the pristine compound (PrFeAsO) exhibited a metallic like step in resistivity below 150K followed by another step at 12K. The former is associated with the spin density wave (SDW) like ordering of Fe spins and later to the anomalous magnetic ordering for Pr moments. Both the resistivity anomalies are absent in case of superconducting PrFeAsO0.8F0.2 sample. Detailed high field (up to 12Tesla) electrical and magnetization measurements are carried out for superconducting PrFeAsO0.8F0.2 sample. The PrFeAsO0.8F0.2 exhibited superconducting onset (Tconset) at around 47K with Tc(ρ =0) at 38K. Though the Tconset remains nearly invariant, the Tc(ρ =0) is decreased with applied field, and the same is around 23K under applied field of 12Tesla. The upper critical field (Hc2) is estimated from the Ginzburg Landau equation (GL) fitting, which is found to be ~ 182Tesla. Critical current density (Jc) being calculated from high field isothermal magnetization (MH) loops with the help of Beans critical state model, is found to be of the order of 103 A/cm2. Summarily, the superconductivity characterization of single step synthesised PrFeAsO0.8F0.2 superconductor is presented.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
PrFeAsO0.8F0.2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	47	Pressure not reported	onset
PrFeAsO0.8F0.2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	38	Pressure not reported	zero_resistance
PrFeAsO0.8F0.2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	23	Pressure not reported	zero_resistance
PrFeAsO0.8F0.2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown