Strongly enhanced current densities in Sr0.6K0.4Fe2As2 superconducting tapes
He Lin, Chao Yao, Xianping Zhang, Haitao Zhang, Dongliang Wang, Qianjun Zhang, Yanwei Ma, Satoshi Awaji, Kazuo Watanabe
arXiv:1309.7618 · DOI 10.1038/srep04465 · 2013-09-29 · Scientific Reports
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Improving transport current has been the primary issue for practical application of superconducting wires and tapes. However, the porous nature of powder-in-tube (PIT) processed iron-based superconducting tapes is thought to be one of the important reasons for the low Jc values. In this work, the superconducting core density of ex-situ Sr0.6K0.4Fe2As2 tapes was significantly improved by employing a simple hot pressing as an alternative route for final sintering. At 4.2 K, the transport Jc values showed excellent values of 5.1x10^4 A/cm^2 at 10 T and 4.3x10^4 A/cm^2 at 14 T, respectively, which attain the Jc level desired for practical applications. Moreover, the Jc values exhibited extremely weak magnetic field dependence. These results clearly demonstrate that PIT pnictide wire conductors are very promising for high field magnet applications.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| Sr0.6K0.4Fe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | — |
Similar papers
Realization of practical level current densities in Sr0.6K0.4Fe2As2 tape conductors for high-field applications
similarity 0.94Xianping Zhang et al. · 2014 · arXiv:1403.6704
Source status unknown — claims are unverified
High critical current density and low anisotropy in textured Sr1-xKxFe2As2 tapes for high field applications
similarity 0.94Zhaoshun Gao et al. · 2013 · arXiv:1302.4583
Source status unknown — claims are unverified
Evidence for superior current carrying capability of iron pnictide tapes under hydrostatic pressure
similarity 0.93Babar Shabbir et al.
Source status unknown — claims are unverified
Hot pressing to enhance the transport Jc of Sr0.6K0.4Fe2As2 superconducting tapes
similarity 0.93He Lin et al. · 2014 · arXiv:1408.4516
Source status unknown — claims are unverified
Large transport critical currents of powder-in-tube Sr0.6K0.4Fe2As2/Ag superconducting wires and tapes
similarity 0.92Lei Wang et al. · 2009 · arXiv:0911.3701
Source status unknown — claims are unverified
Achievement of practical level critical current densities in PIT Ba1-xKxFe2As2/Ag tapes by conventional cold mechanical deformation
similarity 0.92Zhaoshun Gao et al. · 2013 · arXiv:1310.4623
Source status unknown — claims are unverified