Stabilization of high-Tc phase of BiS2-based superconductor LaO0.5F0.5BiS2 using high-pressure synthesis
Yoshikazu Mizuguchi, Takafumi Hiroi, Joe Kajitani, Hiroshi Takatsu, Hiroaki Kadowaki, Osuke Miura
arXiv:1402.5189 · DOI 10.7566/JPSJ.83.053704 · 2014-02-21 · Journal of the Physical Society of Japan
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
High-quality polycrystalline samples of LaO0.5F0.5BiS2 were obtained using high-pressure synthesis technique. The LaO0.5F0.5BiS2 sample prepared by heating at 700 C under 2 GPa showed superconductivity with superconducting transition temperatures (Tc) of Tconset = 11.1 and Tczero = 8.5 K in the electrical resistivity measurements and Tconset = 11.5 and Tcirr = 9.4 K in the magnetic susceptibility measurements, which are obviously higher than those of the LaO0.5F0.5BiS2 polycrystalline samples obtained using conventional solid-state reaction. It was found that the high-Tc phase can be stabilized under high pressure and relatively-low annealing temperature. X-ray diffraction analysis revealed that the high-Tc phase possessed a small ratio of lattice constants of a and c, c/a.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| LaO0.5F0.5BiS2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 11.1 | 2 GPa | onset |
| LaO0.5F0.5BiS2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 8.5 | 2 GPa | zero_resistance |
| LaO0.5F0.5BiS2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 11.5 | 2 GPa | onset |
| LaO0.5F0.5BiS2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 9.4 | 2 GPa | unknown |
Similar papers
Increase in Tc and change of crystal structure by high-pressure annealing in BiS2-based superconductor CeO0.3F0.7BiS2
similarity 0.91Joe Kajitani et al. · 2014 · arXiv:1404.6361
Source status unknown — claims are unverified
Anisotropic two-gap superconductivity and the absence of a Pauli paramagnetic limit in single-crystalline LaOFBiS
similarity 0.90Y. C. Chan et al. · 2017 · arXiv:1710.10841
Source status unknown — claims are unverified
Effect of high pressure annealing on the normal state transport of LaO0.5F0.5BiS2
similarity 0.90I. Pallecchi et al. · 2014 · arXiv:1405.3832
Source status unknown — claims are unverified
Effect of yttrium substitution on the superconducting properties of La1−xYxO0.5F0.5BiS2
similarity 0.89I. Jeon et al.
Source status unknown — claims are unverified
Investigation of the phonon dispersion associated with superlattice reflections in the BiS2-based superconductor LaBiS2O0.5F0.5
similarity 0.89Hiromu Tamatsukuri et al.
Source status unknown — claims are unverified
Investigation of superconductivity in Ce-doped (La,Pr)OBiS2 single crystals
similarity 0.89Masanori Nagao et al. · 2022 · arXiv:2204.08904
Source status unknown — claims are unverified