Enhancement of Superconducting Transition Temperature Due to Antiferromagnetic Spin Fluctuations in Iron-pnictides LaFe(As_{1-x}P_x)(O_{1-y}F_y) : 31P-NMR Studies

H. Mukuda; F. Engetsu; K. Yamamoto; K. T. Lai; M. Yashima; Y. Kitaoka; A. Takemori; S. Miyasaka; S. Tajima

doi:10.1103/PhysRevB.89.064511

← Back to search

Enhancement of Superconducting Transition Temperature Due to Antiferromagnetic Spin Fluctuations in Iron-pnictides LaFe(As_{1-x}P_x)(O_{1-y}F_y) : 31P-NMR Studies

H. Mukuda, F. Engetsu, K. Yamamoto, K. T. Lai, M. Yashima, Y. Kitaoka, A. Takemori, S. Miyasaka, S. Tajima

arXiv:1402.5220 · DOI 10.1103/PhysRevB.89.064511 · 2014-02-21 · Physical Review B

T3theoretical16 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Systematic P-NMR studies on LaFe(As_{1-x}P_x)(O_{1-y}F_y) with y=0.05 and 0.1 have revealed that the antiferromagnetic spin fluctuations (AFMSFs) at low energies are markedly enhanced around x=0.6 and 0.4, respectively, and as a result, Tc exhibits respective peaks at 24 K and 27 K against the P-substitution for As. This result demonstrates that the AFMSFs are responsible for the increase in Tc for LaFe(As_{1-x}P_x)(O_{1-y}F_y) as a primary mediator of the Cooper pairing. From a systematic comparison of AFMSFs with a series of (La_{1-z}Y_z)FeAsO_δ compounds in which Tc reaches 50 K for z=0.95, we remark that a moderate development of AFMSFs causes the Tc to increase up to 50 K under the condition that the local lattice parameters of FeAs tetrahedron approaches those of the regular tetrahedron. We propose that the T_c of Fe-pnictides exceeding 50 K is maximized under an intimate collaboration of the AFMSFs and other factors originating from the optimization of the local structure.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
LaFe(As0.6P0.4)(O0.9F0.1) Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	27	Pressure not reported	onset
LaFe(As0.2P0.8)(O0.9F0.1) Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	8.8	Pressure not reported	onset
LaFeP(O0.9F0.1) Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	5.4	Pressure not reported	onset
LaFe(As0.6P0.4)(O0.95F0.05) Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	19	Pressure not reported	onset
LaFe(As0.4P0.6)(O0.95F0.05) Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	24	Pressure not reported	onset
LaFeP(O0.95F0.05) Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	6.7	Pressure not reported	onset
Y0.95La0.05FeAsOδ Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	50	Pressure not reported	unknown
LaFeAsO0.9F0.1 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	26	Pressure not reported	unknown
SmFeAsO Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	55	Pressure not reported	unknown
LaFePO Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	4	Pressure not reported	unknown
Ba0.6K0.4Fe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	38	Pressure not reported	unknown
Ca4(Mg,Ti)3Fe2As2O8-y Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	47	Pressure not reported	unknown
Sr4(Mg0.3Ti0.7)2O6Fe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	34	Pressure not reported	unknown
Y0.2La0.8FeAsOδ Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	34	Pressure not reported	unknown
LaFeAsOδ Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	28	Pressure not reported	unknown