Anisotropic upper critical field of BiS2-based superconductor LaO0.5F0.5BiS2
Yoshikazu Mizuguchi, Atsushi Miyake, Kazuto Akiba, Masashi Tokunaga, Joe Kajitani, Osuke Miura
arXiv:1404.3798 · DOI 10.1103/PhysRevB.89.174515 · 2014-04-15 · Physical Review B
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Superconducting properties under high magnetic fields for the novel BiS2-based layered superconductor LaO0.5F0.5BiS2 (polycrystalline sample prepared using the high-pressure synthesis method) have been investigated. The anisotropy of the upper critical field was discussed by analyzing the temperature dependence of the temperature derivative of resistivity. The temperature dependence of upper critical field showed an anomalous behavior with a characteristic magnetic field of 8 T. We revealed that the anomalous behavior was caused by the existence of three kinds of upper critical field, HC2max, HC2mid and HC2min in LaO0.5F0.5BiS2. The lowest upper critical field HC2min is regarded as the Hc2 where the superconducting states of the grains with an orientation of H // c are suppressed. The HC2max and HC2mid are regarded as the Hc2 where the superconducting states of the grains with an orientation of H // ab are suppressed. The difference between the HC2max and HC2mid could be explained by the anisotropy of superconducting states within the Bi-S plane. The estimated anisotropy parameter of the upper critical fields was about 7.4 for the high-pressure-synthesized LaO0.5F0.5BiS2 polycrystalline sample. Since the value was clearly lower than the anisotropy parameter of over 30 observed in the previous report on the LaO0.5F0.5BiS2 single crystals grown under ambient pressure, we concluded that a larger anisotropy of superconductivity was not essential for the enhancement of Tc, and lower anisotropy might be important for a higher Tc in LaO1-xFxBiS2.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| LaO0.5F0.5BiS2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
Upper critical magnetic field of OFBiS ( = La, Nd) superconductors at ambient and high pressure
similarity 0.93Fang, Y. et al. · 2017 · arXiv:1611.03926
Source status unknown — claims are unverified
The upper critical field and its anisotropy in LiFeAs
similarity 0.90J. L. Zhang et al. · 2011 · arXiv:1101.3159
Source status unknown — claims are unverified
Anisotropic two-gap superconductivity and the absence of a Pauli paramagnetic limit in single-crystalline LaOFBiS
similarity 0.90Y. C. Chan et al. · 2017 · arXiv:1710.10841
Source status unknown — claims are unverified
Upper critical field and thermally activated flux flow in single crystalline TlRbFeSe
similarity 0.90L. Jiao et al. · 2011 · arXiv:1106.2283
Source status unknown — claims are unverified
Upper Critical Fields and Anisotropy of Ca1-xLaxFe2As2 Single Crystals
similarity 0.89W. Zhou et al. · 2013 · arXiv:1308.5734
Source status unknown — claims are unverified
Upper critical field, critical current density and activation energy of the new La1-xSmxOF0.5BiS2 (x = 0.2, 0.8) superconductor
similarity 0.89G. Kalai Selvan et al. · 2015 · arXiv:1507.06247
Source status unknown — claims are unverified