Molybdenum-Rhenium superconducting suspended nanostructures

Mohsin Aziz; David Christopher Hudson; Saverio Russo

doi:10.1063/1.4883115

← Back to search

Molybdenum-Rhenium superconducting suspended nanostructures

Mohsin Aziz, David Christopher Hudson, Saverio Russo

arXiv:1406.0653 · DOI 10.1063/1.4883115 · 2014-06-03 · Applied Physics Letters

T1theoretical21 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Suspended superconducting nanostructures of MoRe $50\%/50\%$ by weight are fabricated employing commonly used fabrication steps in micro- and nano-meter scale devices followed by wet-etching with Hydro-fluoric acid of a SiO$_2$ sacrificial layer. Suspended superconducting channels as narrow as $50\,\rm{nm}$ and length $3\,\rm{μm}$ have a critical temperature of $\approx 6.5\,\rm{K}$, which can increase by $0.5\rm{K}$ upon annealing at $400\,^{\circ}\mathrm{C}$. A detailed study of the dependence of the superconducting critical current and critical temperature upon annealing and in devices with different channel width reveals that desorption of contaminants is responsible for the improved superconducting properties. These findings pave the way for the development of superconducting electromechanical devices using standard fabrication techniques.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
MoRe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	6.5	Pressure not reported	unknown
MoRe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	7	Pressure not reported	unknown
MoRe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	6	Pressure not reported	unknown
MoRe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	9	Pressure not reported	unknown
MoRe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	7.5	Pressure not reported	unknown
Mo50Re50 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	15	Pressure not reported	unknown
Mo60Re40 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	5.6	Pressure not reported	unknown
Mo60Re40 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	9.7	Pressure not reported	unknown