Synthesis and post-annealing effects of alkaline-metal-ethylenediamine-intercalated superconductors Ax(C2H8N2)yFe2-zSe2 (A = Li, Na) with Tc = 45 K
Takashi Noji, Takehiro Hatakeda, Shohei Hosono, Takayuki Kawamata, Masatsune Kato, Yoji Koike
arXiv:1408.0346 · DOI 10.1016/j.physc.2014.01.007 · 2014-08-02 · Physica C-superconductivity and Its Applications
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
New iron-based intercalation superconductors Ax(C2H8N2)yFe2-zSe2 (A = Li, Na) with Tc = 45 K have successfully been synthesized via intercalation of dissolved alkaline metal in ethylenediamine. The c-axis lengths of Ax(C2H8N2)yFe2-zSe2 (A = Li, Na) are 20.74(7) Å and 21.9(1) Å, respectively, and are about 50 % larger than that of KxFe2Se2, indicating that not only alkaline metal but also ethylenediamine is intercalated between the Se-Se layers of FeSe. It seems that the high-Tc of Ax(C2H8N2)yFe2-zSe2 (A = Li, Na) is caused by the possible two-dimensional electronic structure due to the large c-axis length. Through the post-annealing in an evacuated glass tube, it has been found that Tc decreases with increasing post-annealing temperature and that deintercalation of EDA from the as-intercalated sample takes place at low temperatures below 250 °C.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| Lix(C2H8N2)yFe2-zSe2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 45 | Pressure not reported | unknown |
| Nax(C2H8N2)yFe2-zSe2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 45 | Pressure not reported | unknown |
Similar papers
New Li-Ethylenediamine-Intercalated Superconductor Li(CHN)FeSe with = 45 K
similarity 0.93Takehiro Hatakeda et al. · 2013 · arXiv:1311.0141
Source status unknown — claims are unverified
Preparation of new superconductors by metal doping of two-dimensional layered materials using ethylenediamine
similarity 0.92Xiao Miao et al.
Source status unknown — claims are unverified
Observation of superconductivity at 30 K~46 K in AxFe2Se2 (A = Li, Na, Ba, Sr, Ca, Yb, and Eu)
similarity 0.90T. P. Ying et al. · 2012 · arXiv:1202.4340
Source status unknown — claims are unverified
Two-gap superconducting properties of alkaline-earth intercalated (A = Ba or Sr)
similarity 0.89Yung-Yuan Hsu et al. · 2015 · arXiv:1509.06455
Source status unknown — claims are unverified
Emergence of magnetism and controlling factors of superconductivity in Li/Na-ammonia cointercalated FeSe1−zTez
similarity 0.89Hechang Lei (雷和畅) et al.
Source status unknown — claims are unverified
New intercalation superconductor Lix(C6H16N2)yFe2-zSe2 with a very large interlayer-spacing and Tc = 38 K
similarity 0.89S. Hosono et al. · 2015 · arXiv:1510.08625
Source status unknown — claims are unverified