Flux growth utilizing the reaction between flux and crucible
J. -Q. Yan
arXiv:1501.03770 · DOI 10.1016/j.jcrysgro.2015.01.017 · 2015-01-15 · Journal of Crystal Growth
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Flux growth involves dissolving the components of the target compound in an appropriate flux at high temperatures and then crystallizing under supersaturation controlled by cooling or evaporating the flux. A refractory crucible is generally used to contain the high temperature melt. The reaction between the melt and crucible materials can modify the composition of the melt, which typically results in growth failure, or contaminates the crystals. Thus one principle in designing a flux growth is to select suitable flux and crucible materials thus to avoid any reaction between them. In this paper, we review two cases of flux growth in which the reaction between flux and Al$_2$O$_3$ crucible tunes the oxygen content in the melt and helps the crystallization of desired compositions. For the case of La$_5$Pb$_3$O, Al$_2$O$_3$ crucible oxidizes La to form a passivating La$_2$O$_3$ layer which not only prevents further oxidization of La in the melt but also provides [O] to the melt. For the case of La$_{0.4}$Na$_{0.6}$Fe$_2$As$_2$, it is believed that the Al$_2$O$_3$ crucible reacts with NaAsO$_2$ and the reaction consumes oxygen in the melt thus maintaining an oxygen-free environment.
Similar papers
Magnetic and structural transitions in LaNaFeAs single crystals
similarity 0.88J. -Q. Yan et al. · 2014 · arXiv:1412.7447
Source status unknown — claims are unverified
Structural transition and possible pressure-induced superconductivity in a suboxide LaPbO
similarity 0.86Jiaqiang Yan et al. · 2025 · arXiv:2508.10080
Source status unknown — claims are unverified
Single Crystal Growth and Characterization of the Iron-Based Superconductor KFe2As2 Synthesized by KAs Flux Method
similarity 0.86Kunihiro Kihou et al. · 2010 · arXiv:1009.4002
Source status unknown — claims are unverified
A comprehensive scenario of the single crystal growth and doping dependence of resistivity and anisotropic upper critical fields in (BaK)FeAs ()
similarity 0.86Y. Liu et al. · 2014 · arXiv:1403.0227
Source status unknown — claims are unverified
Single-crystal growth of iron-based superconductor LaNaFeAs
similarity 0.85Yanhong Gu et al. · 2018 · arXiv:1805.08923
Source status unknown — claims are unverified
Crystal growth and characterization of a hole-doped iron-based superconductor Ba(FeTi)As
similarity 0.85Yi-Li Sun et al. · 2026 · arXiv:2601.14981
Source status unknown — claims are unverified