Cubic H$_3$S around 200 GPa: an atomic hydrogen superconductor stabilized by sulfur

D. A. Papaconstantopoulos; B. M. Klein; M. J. Mehl; W. E. Pickett

doi:10.1103/PhysRevB.91.184511

← Back to search

Cubic H$_3$S around 200 GPa: an atomic hydrogen superconductor stabilized by sulfur

D. A. Papaconstantopoulos, B. M. Klein, M. J. Mehl, W. E. Pickett

arXiv:1501.03950 · DOI 10.1103/PhysRevB.91.184511 · 2015-01-16 · Physical Review B

T1theoretical132 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

The multiple scattering-based theory of Gaspari and Gyorffy for the electron-ion matrix element in close packed metals is applied to Im-3m H3S, which has been predicted by Duan {\it et al.} and Bernstein {\it et al} to be the stable phase at this stoichiometry around 190 GPa, thus is the leading candidate to be the phase observed to superconduct at 190K by Drozdov, Eremets, and Troyan. The nearly perfect separation of vibrational modes into those of S and of H character provides a simplification that enables identification of contributions of the two atoms separately. The picture that arises is basically that of superconducting atomic H stabilized by strong covalent mixing with S 3p and "3d" character. The reported isotope shift is much larger than the theoretical one,suggesting there is large anharmonicity in the H vibrations. Given the relative unimportance of sulfur, hydrides of lighter atoms at similarly high pressures may also lead to high temperature superconductivity.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
H3S Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	190	190 GPa	unknown
H2S Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	190	200 GPa	unknown
Li Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	25	Pressure not reported	unknown
Ca Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	25	Pressure not reported	unknown
Si Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	14	Pressure not reported	unknown
H2S Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	40	140 GPa	unknown
H2S Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	80	160 GPa	unknown
H3S Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	200	200 GPa	unknown
PdH Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure unresolved	unknown
H3S Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	234	210 GPa	unknown
H3S Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	215	210 GPa	unknown
H3S Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	170	210 GPa	unknown
H3S Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	90	Pressure not reported	unknown