High temperature superconductivity in sulfur and selenium hydrides at high pressure

José A. Flores-Livas; Antonio Sanna; E. K. U. Gross

High temperature superconductivity in sulfur and selenium hydrides at high pressure

José A. Flores-Livas, Antonio Sanna, E. K. U. Gross

arXiv:1501.06336 · 2015-01-26

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Due to its low atomic mass hydrogen is the most promising element to search for high-temperature phononic superconductors. However, metallic phases of hydrogen are only expected at extreme pressures (400 GPa or higher). The measurement of a record superconducting critical temperature of 190 K in a hydrogen-sulfur compound at 200 GPa of pressure[1], shows that metallization of hydrogen can be reached at significantly lower pressure by inserting it in the matrix of other elements. In this work we re-investigate the phase diagram and the superconducting properties of the H-S system by means of minima hopping method for structure prediction and Density Functional theory for superconductors. We also show that Se-H has a similar phase diagram as its sulfur counterpart as well as high superconducting critical temperature. We predict SeH3 to exceed 120 K superconductivity at 100 GPa. We show that both SeH3 and SH3, due to the critical temperature and peculiar electronic structure, present rather unusual superconducting properties.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
H3S Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	190	200 GPa	unknown
H3S Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	180	200 GPa	unknown
H3S Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	185	177 GPa	unknown
D3S Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	141	200 GPa	unknown
D3S Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	90	Pressure not reported	unknown
H3S Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	195	180 GPa	unknown
SeH3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	131	200 GPa	unknown
SeH3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	110	150 GPa	unknown
SeH3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	123	100 GPa	unknown